Investigation of a new lead-free Bi0.5(Na0.40K0.10)TiO3-(Ba0.7Sr0.3)TiO3 piezoelectric ceramic
نویسندگان
چکیده
Lead-free piezoelectric compositions of the (1-x)Bi0.5(Na0.40K0.10)TiO3-x(Ba0.7Sr0.3)TiO3 system (when x = 0, 0.05, 0.10, 0.15, and 0.20) were fabricated using a solid-state mixed oxide method and sintered between 1,050°C and 1,175°C for 2 h. The effect of (Ba0.7Sr0.3)TiO3 [BST] content on phase, microstructure, and electrical properties was investigated. The optimum sintering temperature was 1,125°C at which all compositions had densities of at least 98% of their theoretical values. X-ray diffraction patterns that showed tetragonality were increased with the increasing BST. Scanning electron micrographs showed a slight reduction of grain size when BST was added. The addition of BST was also found to improve the dielectric and piezoelectric properties of the BNKT ceramic. A large room-temperature dielectric constant, εr (1,609), and piezoelectric coefficient, d33 (214 pC/N), were obtained at an optimal composition of x = 0.10.
منابع مشابه
LEAD-FREE BNKT PIEZOELECTRIC ACTUATOR
An actuator is a device that converts input energy into mechanical energy. According to various types of input energy, various actuators have been advanced. Displacement in the electromagnetic, hydraulic and pneumatic actuators achieve by moving a piston via electromagnetic force or pressure, however the piezoelectric actuator (piezoceramic plates) displace directly. Therefore, accuracy and spe...
متن کاملGiant Strains in Non-Textured (Bi1/2 Na1/2 )TiO3 -Based Lead-Free Ceramics.
Giant electric-field-induced strain of 0.70%, corresponding to a d33 * value of 1400 pm V(-1) , is observed in a lead-free (Bi1/2 Na1/2 )TiO3 -based polycrystalline ceramic. This is comparable to the properties of single crystals. An in situ transmission electron microscopy study indicates that the excellent performance originates from phase transitions under the applied electric fields.
متن کاملEffect of uniaxial stress on ferroelectric behavior of (Bi1/2Na1/2)TiO3-based lead-free piezoelectric ceramics
Prior studies have shown that a field-induced ferroelectricity in ceramics with general chemical formula (1−x−y)(Bi1/2Na1/2)TiO3–xBaTiO3–y(K0.5Na0.5)NbO3 and a very low remanent strain can produce very large piezoelectric strains. Here we show that both the longitudinal and transverse strains gradually change with applied electric fields even during the transition from the nonferroelectric to t...
متن کاملDevelopment, Characterization, and Piezoelectric Fatigue Behavior of Lead- Free Perovskite Piezoelectric Ceramics
The development of lead-free perovskite piezoelectrics as environmentally compatible alternatives to lead zirconate titanate (PZT) has received significant attention recently. Two main categories of lead free perovskite piezoelectric ceramic systems were investigated as potential replacements to lead zirconate titantate (PZT) for actuator devices. First, solid solutions based on Li, Ta, and Sb ...
متن کاملProcessing and Characterization of Microwave Dielectric Ceramics and Thin Films-Nd2(Ti2/3Al1/3)3O9-δ and (Ba0.7Sr0.3)TiO3
Reactive powders of stoichiometry Nd2(Ti2/3Al1/3)3O9-δ and thin films of (Ba0.7Sr0.3)TiO3 have been prepared by the conventional mixed-oxide method and the metal-organic deposition method, respectively. The corresponded phases after calcination and sintering are investigated by XRD diffraction. Single phase of Nd2(Ti2/3Al1/3)3O9-δ could be only obtained by sintering over 1400C for 4 h. (Ba0.7Sr...
متن کامل