Tribosynthesis of Fe3−xMnxC Phases via Mechanical Alloying and Annealing
نویسندگان
چکیده
Powderous crystalline materials of the composition Fe3−xMnxC have been prepared by first synthesizing Fe3C via mechanical alloying in a planetary mill followed by the addition of elemental manganese and arc-plasma melting or via the classic ceramic route in an electric furnace. The milling time for the synthesis of Fe3C was significantly reduced through adjusting the parameters of the planetary ball mill. When the ball-to-powder ratio was lowered, significantly larger batches were possible. Sintering in a fired tubular furnace was found to be the method of choice for the aftertreatment of the nanocrystalline Fe3−xMnxC powders as exemplified by X-ray Rietveld refinements.
منابع مشابه
The Effect of Impurity of Inert Atmosphere on Synthesis of Nanostructure TiAl (γ) Alloy by Mechanical Alloying Process
In this research, the high-energy planetary mill was employed to produce nanocrystalline Ti-50Al(γ)(at%) powders. Initial powders were mechanically alloyed in 99.9999% and 90% purities of Argon and also Air atmosphere with alloying times up to 50h. The effect of impurity of Argon atmosphere on the microstructure and the rate of phase transformation of Ti-50Al were investigated during mechanical...
متن کاملEffect of Chromium Content on Formation of (Mo1-x-Crx) Si2 Nanocomposite Powders via Mechanical Alloying
(Mo1-x-Crx)Si2 composite powders were successfully synthesized by ball milling of Mo, Cr and Si elemental powders. Effects of the Cr content, milling time and annealing temperature were investigated. X-ray diffraction (XRD) was used to characterize the milled and annealed powders. The morphological and microstructural evolutions were studied by scanning electron microscopy (SEM) and transmissio...
متن کاملSynthesis and thermal stability of nanocrystalline Mg-6Al-1Zn-1Si alloy prepared via mechanical alloying
Thermal stability and the kinetics of the grain growth of nano-crystalline Mg-6Al-1Zn-1Si alloy prepared via mechanical alloying (MA) were investigated. It started with elemental powders, using a variety of analytical techniques including differential scanning calorimetry (DSC), X-ray diffraction method (XRD), and scanning electron microscopy (SEM) coupled with energy dispersive spectrometry (E...
متن کاملStudying the Effect of Productive Factors on Synthesis of Anostructure Tial (Γ) Alloy By Mechanical Alloying
In this research, the Planetary mill was used for mechanical alloying (MA) of Ti and Alpowder mixture with equal at% (Ti50Al50). The effect of various factors, such as process control agent(PCA), speed of rotation of vial and ball-to-powder weight ratio, on process were studied and the bestcondition to synthesis the alloy was determined. Study on X-ray diffraction (XRD) patterns showedthat at p...
متن کاملA Comparison between the Effect of Cr and W Addition on Formation Kinetic of Nanostructure TiAl(γ) Alloy by Mechanical Alloying Route
In this research, mechanical alloying was used to produce Ti-50Al, Ti-45Al-5Cr and Ti-45Al-5W (at%) alloys. The effect of ternary addition (Cr and W) on microstructure and production efficiency of TiAl alloy were investigated. Alloying was performed in a planetary mill and the milling time varying from 5 to 70h. The structural evaluation in these powders was done by X-ray diffraction (XRD) tech...
متن کامل