Origins of 1/f noise in nanostructure inclusion polymorphous silicon films
نویسندگان
چکیده
In this article, we report that the origins of 1/f noise in pm-Si:H film resistors are inhomogeneity and defective structure. The results obtained are consistent with Hooge's formula, where the noise parameter, αH, is independent of doping ratio. The 1/f noise power spectral density and noise parameter αH are proportional to the squared value of temperature coefficient of resistance (TCR). The resistivity and TCR of pm-Si:H film resistor were obtained through linear current-voltage measurement. The 1/f noise, measured by a custom-built noise spectroscopy system, shows that the power spectral density is a function of both doping ratio and temperature.
منابع مشابه
Morphological, structural and photoresponse characterization of ZnO nanostructure films deposited on plasma etched silicon substrates
ZnO nanostructure films were deposited by radio frequency (RF) magnetron sputtering on etched silicon (100) substrates using dry Ar/SF6 plasma, at two etching times of 5 min and 30 min, and on non etched silicon surface. Energy dispersive X-ray (EDX) technique was employed to investigate the elements contents for etched substrates as well as ZnO films, where it is found to be stoichiometric. Su...
متن کاملPolymorphous Si thin films from radio frequency plasmas of SiH4 diluted in Ar: A study by transmission electron microscopy and Raman spectroscopy
In this study, we present a detailed structural characterization by means of transmission electron microscopy and Raman spectroscopy of polymorphous silicon ~pm-Si:H! thin films deposited using radio-frequency dust-forming plasmas of SiH4 diluted in Ar. Square-wave modulation of the plasma and gas temperature was varied to obtain films with different nanostructures. Transmission electron micros...
متن کاملPlasma production of nanocrystalline silicon particles and polymorphous silicon thin films for large-area electronic devices*
Powder formation in silane plasmas has been considered as a technology drawback because it might lead to the formation of macroscopic defects in the deposited layers. Here we summarize our recent efforts in controlling the formation of powder precursors, in particular, nanocrystalline silicon particles, aiming at their incorporation in the films. Indeed, the incorporation of clusters and crysta...
متن کاملEffect of Grain Size and Hydrogen Passivation on the Electrical Properties of Nanocrystalline Silicon Films
The properties of mixed-phase (nanocrystalline/amorphous) silicon layers produced by reactive RF-sputtering are described. The chemical composition and nanostructure [i.e. nanocrystal (NC) size and volume fraction] of the films were studied by Rutherford backscattering spectroscopy (RBS) and micro-Raman spectroscopy, respectively. Samples with different fractions of the nanocrystalline phase an...
متن کاملLong-range fluctuations of random potential landscape as a mechanism of 1/f noise in hydrogenated amorphous silicon
We describe a mechanism, which links the long-range potential fluctuations induced by charged defects to the low frequency resistance noise widely known as 1/f noise. This mechanism is amenable to the first principles microscopic calculation of the noise spectrum, which includes the absolute noise intensity. We have performed such a calculation for the thin films of hydrogenated amorphous silic...
متن کامل