Shear bond strength of composite resin to titanium according to various surface treatments

نویسندگان

  • Seung-Yun Lee
  • Mong-Sook Vang
  • Hong-So Yang
  • Sang-Won Park
  • Ha-Ok Park
  • Hyun-Pil Lim
چکیده

STATEMENT OF PROBLEM When veneering composite resin-metal restoration is prepared, the fact that bond strength between Ti and composite resin is relatively weak should be considered. PURPOSE The purpose of this study is to evaluate the shear bond strength between the veneering composite resin and commercial pure (CP) Ti / Ti-6Al-4V alloy according to the method of surface treatment. MATERIAL AND METHODS The disks were cast by two types of metal. Their surfaces were treated by sandblasting, metal conditioner, TiN coating and silicoating respectively. After surface treatment, the disks were veneered by composite resin (Tescera™, Bisco, USA) which is 5 mm in diameter and 3 mm in thickness. The specimens were stored in water at 25℃ for 24 hours, and then evaluated for their shear bond strength by universal testing machine (STM-5®, United Calibration, USA). These values were statistically analyzed. RESULTS 1. All methods of surface treatment were used in this study satisfied the requirements of ISO 10477 which is the standard of polymer-based crown and bridge materials. 2. The metal conditioner treated group showed the highest value in shear bond strength of CP Ti, silicoated group, TiN coated group, sandblasted group, in following order. 3. The silicoated group showed the highest value in shear bond strength of Ti-6Al-4V alloy, metal conditioner treated group, sandblasted group, TiN coated group, in following order. CONCLUSION Within the limitations of this study, all methods of surface treatment used in this study are clinically available.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Comparison of Shear Bond Strength of Silorane and Methacrylate-Based Composites to IPS Empress 2 Ceramic with Various Surface Treatments

Objectives: Treatment of chipped or fractured porcelain with composite resin is considered as an economic treatment for minor fractures in ceramics. The aim of this study was to evaluate the effect of different ceramic surface treatments on bond strength of methacrylate-based and silorane-based composite resin to IPS Empress 2. Methods: Sixty IPS Empress 2 ceramic discs were fabrica...

متن کامل

Effects of Various Chairside Surface Treatments on Zirconia-Resin Cement Bond Strength

Introduction: Various surface treatments have been used to improve the adhesion of resin cement to zirconia restorations. The present study aimed to investigate the effects of different surface treatments on the bond strength of resin cement to zirconia (Y-TZP) in clinical practice. Methods: thirty square Y-TZP samples were classified into three groups of 10, including group SB (50 µm sandblast...

متن کامل

In vitro evaluation of the effect of different surface treatments and bonding systems on shear bond strength of composite veneer to Stainless Steel Crown

Abstract   Background and aim: Using Stainless Steel Crowns (SSC) for Early Childhood Caries usually causes an unpleasant condition in the aesthetic of the patients. The aim of this study was to evaluate the effect of different surface treatments and bonding systems on shear bond strength of composite veneer to Stainless Steel Crown. Materials and Methods: In this in vitro study, 120 SSC were ...

متن کامل

The Effects of Different Surface Treatments on the Shear Bond Strength of Composite Resin to Machined Titanium

THE EFFECTS OF DIFFERENT SURFACE TREATMENTS ON THE SHEAR BOND STRENGTH OF COMPOSITE RESIN TO MACHINED TITANIUM Mohammad AlJadi, D.D.S. Marquette University, 2011 Purpose: The purpose of this study was to evaluate the shear bond strength between machined titanium and composite resin using different surface treatments. Materials and Methods: Titanium (Ti-6Al-4V) specimens were ground with 600 gri...

متن کامل

Micro-Shear Bond Strength of Indirect Composite Resin to Three Different Computer-Milled Cores After Thermocycling

Background and Aim: The aim of this study was to evaluate the micro-shear bond strength of an indirect composite resin to three different types of cores. Materials and Methods: In this in-vitro study, 14 blocks (5×5×2 mm) were designed and milled by computer from cobalt-chromium (Co-Cr) alloy, zirconia, and polyether ether ketone (PEEK). Each sample was treated according to the manufacturer’s ...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 1  شماره 

صفحات  -

تاریخ انتشار 2009