In Situ Thermographic Imaging of Shear Bands During Tensile Testing
نویسندگان
چکیده
Uniaxial tensile tests were conducted on a Zr-based bulk metallic glass (BMG) with a nominal composition of Zr52.5Cu17.9Ni14.6Al10.0Ti5.0 (at.%). An infrared (IR) camera was utilized in situ during tensile testing to observe shear band evolution and fracture in the BMG. This unique visualization technique revealed that the temperature along the axis of shear band propagation constantly decreases from the point of initiation to arrest.
منابع مشابه
Modeling the Dynamic Propagation of Shear Bands in Bulk Metallic Glasses
A model is developed for quantifying shear-band propagation in bulk metallic glasses. This model is written in terms of the stress, temperature, and band propagation speed. The model quantifies the shear-band length, width, and speed, as well as the direction of propagation and the magnitude of displacement across the band. Corresponding author: B.J. Edwards, [email protected] (865) 9...
متن کاملDetailed Microstructural Evolutions of TWIP Steel During Tensile Straining: In situ SEM Observations
Microstructural evolutions of twinning induced plasticity (TWIP) steel during tensile straining were investigated by in situ SEM observations. The results indicated that slip lines and mechanical twins as well as surface relief were increased with increasing strain, resulting in a stepped surface. Additionally, these deformation mechanisms could change the shape of each grain via shear and rota...
متن کاملHOT CRACK FORMATION IN PURE CU AND CU-30%ZN ALLOY DURING IN SITU SOLIDIFICATION
The hot cracking susceptibility can be determined by establishing the transition temperature between brittle and ductile fracture at high temperature tensile testing of in situ solidified samples. High temperature tensile properties were determined for commercial cathodic pure Cu and Cu- 30%Zn alloy. The transition temperatures for pure Cu and Cu-30%Zn were evaluated from ultimate tensile stres...
متن کاملIn-situ observation of damage evolution and fracture in AlSi7Mg0.3 cast alloys
The mechanisms which occur during damage initiation, evolution and crack growth in AlSi7Mg0.3 cast alloys are studied by in-situ tensile testing in a scanning electron microscope. It is shown that microcracks in these alloys are predominantly formed in the Si particles. Shear bands are seen to precede the breaking of the Si particles and the dislocation pile-up mechanism can thus be con®rmed as...
متن کاملDesigning Bulk Metallic Glass Matr ix Composites with High Toughness and Tensile Ductility
Metallic glasses have been the subject of intense scientific study since the 1960s, owing to their unique properties such as high strength, large elastic limit, high hardness, and amorphous microstructure. However, bulk metallic glasses have not been used in the high strength structural applications for which they have so much potential, owing to a highly localized failure mechanism that result...