Micro-Structural Characterization of Si-SiC Ceramic Derived from C/C-SiC Composite
نویسنده
چکیده
The main objective of the present work is to processing the porous Si-SiC ceramic by the oxidation of C/C-SiC composite. Phase studies are performed on the oxidized porous composite to examine the changes due to the high temperature oxidation. Further, various characterization techniques are performed on Si-SiC ceramic in order to study the material’s microstructure.
منابع مشابه
In Situ Formation of SiC/CNT Ceramic Nanocomposite by Phenolic Pyrolysis
In this research, using pyrolysis of phenolic resin in the presence of silicon particles, the SiC ceramic composite is formed. The samples were prepared by introducing 30, 35, 40, 45 and 50 wt% of Si particles to the phenolic resin. The samples were cured at 180°C then carbonized at 1100°C. The final carbonized C/Si composites are hot-pressed at 1500°C in inert atmosphere, which is more than th...
متن کاملFabrication and inspection of C/Cf-ZrB2-ZrC-SiC and C/Cf-ZrB2-SiC composite parts resistant to ablation by pressureless sintering method
In this research, the aim is to achieve strong and ablation-resistant composite parts C / Cf-ZrB2-ZrC-SiC and C / Cf-ZrB2-SiC by non-pressure sintering method. C / Cf-ZrB2-SiC samples were prepared using synthesized ZrB2 and SiC powders between layers of resin-impregnated carbon fabric. After pressing with pressure 5 times at 1600 وC and heat treatment for 2 hours in a controlled atmosphere fur...
متن کاملEFFECT OF NANO SiC ADDITIVE ON MCMB-SiC COMPOSITE FABRICATION VIA MOLTEN SILICON INFILTRATION
C-SiC composites with carbon-based mesocarbon microbeads (MCMB) preforms are new type of highpreformance and high-temperature structural materials for aerospace applications. In this study MCMB-SiC composites with high density (2.41 g.cm-3) and high bending strength (210 MPa,) was prepared by cold isostatic press of mixed mesophase carbon powder derived from mesophase pitch with different amoun...
متن کاملSintering Behavior of Spark Plasma Sintered SiC with Si-SiC Composite Nanoparticles Prepared by Thermal DC Plasma Process
The Si-coated SiC (Si-SiC) composite nanoparticle was prepared by non-transferred arc thermal plasma processing of solid-state synthesized SiC powder and was used as a sintering additive for SiC ceramic formation. Sintered SiC pellet was prepared by spark plasma sintering (SPS) process, and the effect of nano-sized Si-SiC composite particles on the sintering behavior of micron-sized SiC powder ...
متن کاملThe effects of Na & Mg adsorption on the electrical properties of SiCNTs: A DFT study
In the present study we focused on the electronic and structural properties of Na and Mg adsorption on the surface of the (6, 6) armchair SiCNTs. The adsorption energy (Eads), band gap energy (Eg), partial density of state (PDOS), chemical potential (μ), global hardness (η), electrophilicity index (ω), global softness (S), work function values (φ) and work function change (Δφ) are calculated by...
متن کامل