The effect of various sandblasting conditions on surface changes of dental zirconia and shear bond strength between zirconia core and indirect composite resin
نویسندگان
چکیده
PURPOSE To measure the surface loss of dental restorative zirconia and the short-term bond strength between an indirect composite resin (ICR) and zirconia ceramic after various sandblasting processes. MATERIALS AND METHODS Three hundred zirconia bars were randomly divided into 25 groups according to the type of sandblasting performed with pressures of 0.1, 0.2, 0.4 and 0.6 MPa, sandblasting times of 7, 14 and 21 seconds, and alumina powder sizes of 50 and 110 µm. The control group did not receive sandblasting. The volume loss and height loss on zirconia surface after sandblasting and the shear bond strength (SBS) between the sandblasted zirconia and ICR after 24-h immersion were measured for each group using multivariate analysis of variance (ANOVA) and Least Significance Difference (LSD) test (α=.05). After sandblasting, the failure modes of the ICR/zirconia surfaces were observed using scanning electron microscopy. RESULTS The volume loss and height loss were increased with higher sandblasting pressure and longer sandblasting treatment, but they decreased with larger powder size. SBS was significantly increased by increasing the sandblasting time from 7 seconds to 14 seconds and from 14 seconds to 21 seconds, as well as increasing the size of alumina powder from 50 µm to 110 µm. SBS was significantly increased from 0.1 MPa to 0.2 MPa according to the size of alumina powder. However, the SBSs were not significantly different with the sandblasting pressure of 0.2, 0.4 and 0.6 MPa. The possibilities of the combination of both adhesive failure and cohesive failure within the ICR were higher with the increases in bonding strength. CONCLUSION Based on the findings of this study, sandblasting with alumina particles at 0.2 MPa, 21 seconds and the powder size of 110 µm is recommended for dental applications to improve the bonding between zirconia core and ICR.
منابع مشابه
Erratum: The effect of various sandblasting conditions on surface changes of dental zirconia and shear bond strength between zirconia core and indirect composite resin
[This corrects the article on p. 214 in vol. 7, PMID: 26140173.].
متن کاملEvaluation of the Effect of Sandblasting (120 μm) on Shear Bond Strength between Ceramic Veneer and Zirconia Core
Background and Aim: Due to the importance of the bond strength between zirconia core (ZC) and porcelain veneer (PV) as well as the paradox about the functionality of sandblasting on the solidity between those layers, this research aimed to evaluate the effect of sandblasting on the shear bond strength (SBS) between ZC and PV. Materials and Methods: After preparing 20 zirconia discs (7 mm &time...
متن کاملMicro-Shear Bond Strength of Indirect Composite Resin to Three Different Computer-Milled Cores After Thermocycling
Background and Aim: The aim of this study was to evaluate the micro-shear bond strength of an indirect composite resin to three different types of cores. Materials and Methods: In this in-vitro study, 14 blocks (5×5×2 mm) were designed and milled by computer from cobalt-chromium (Co-Cr) alloy, zirconia, and polyether ether ketone (PEEK). Each sample was treated according to the manufacturer’s ...
متن کاملEffect of Laser Irradiation on Bond Strength of Zirconia Ceramic to Self-Adhesive Resin Cement
Background and Aim: Bonding of zirconia to resin cement is challenging, and the zirconia surface requires surface treatment to yield an acceptable bond strength. This study aimed to evaluate the effect of different surface treatments on the bond strength of zirconia to a resin cement. Materials and Methods: In this in-vitro experimental study, 60 zirconia discs measuring 12 mm in diameter an...
متن کاملEffects of Various Chairside Surface Treatments on Zirconia-Resin Cement Bond Strength
Introduction: Various surface treatments have been used to improve the adhesion of resin cement to zirconia restorations. The present study aimed to investigate the effects of different surface treatments on the bond strength of resin cement to zirconia (Y-TZP) in clinical practice. Methods: thirty square Y-TZP samples were classified into three groups of 10, including group SB (50 µm sandblast...