Enhanced Interface Structure and Properties of Titanium Carbonitride-Based Cermets with the Extra Solid Phase Reaction
نویسندگان
چکیده
In this paper, the influence of the extra solid phase reaction on the interface structure and mechanical properties of titanium carbonitride-based cermets were investigated. The extra solid phase reaction in the preparation process of cermets could induce the formation of a core/rim/binder interface with the coherent structure and reinforce the interface bonding strength in cermets. The existence of a coherent structure interface can inhibit crack spread and improve the toughness and abrasion resistance of titanium carbonitride-based cermets significantly. Cermets can exhibit the high hardness Rockwell Hardness A (HRA) 92.3, fracture toughness of 11.6 MPa·m1/2, and transverse rupture strength of 2810 MPa.
منابع مشابه
Enhanced Electrocatalytic Performance for Oxygen Reduction via Active Interfaces of Layer-By-Layered Titanium Nitride/Titanium Carbonitride Structures
Cathode materials always limit the performance of fuel cells while the commercial platinum-based catalysts hardly meet the requirements of low cost, durable and stable. Here a non-precious metal oxygen reduction reaction (ORR) electocatalyst based on titanium nitride/titanium carbonitride hierarchical structures (TNTCNHS) is demonstrated as high activity as Pt/C. In alkaline condition, tuning i...
متن کاملFORMATION AND GROWTH OF TITANIUM ALUMINIDE LAYER AT THE SURFACE OF TITANIUM SHEETS IMMERSED IN MOLTEN ALUMINUM
Abstract: titanium sheets in pure molten aluminum at 750 and X-Ray Diffraction Analysis results, TiAlintermetallic layer thickness increases slowly at primary stages. After that an enhanced growth rate occurs due to layercracking and disruption. Presumably, reaction starts with solving titanium into the molten aluminum causing intitanium super saturation and TiAlintermetallic layer which conseq...
متن کاملThe effect of electron beam welding parameters on the microstructural characteristics and mechanical properties of dissimilar joint between 17-4PH steel and Ti6Al4V alloy
This study aimed to investigate the effect of electron beam welding parameters on the microstructural characteristics and mechanical properties of the dissimilar joint between 17-4PH precipitation hardening stainless steel and Ti6Al4V alloy. For this purpose, the welding of these two alloys was done without an interlayer and with an interlayer of copper with a thickness of 0.8 mm. Two different...
متن کاملThe effect of electron beam welding parameters on the microstructural characteristics and mechanical properties of dissimilar joint between 17-4PH steel and Ti6Al4V alloy
This study aimed to investigate the effect of electron beam welding parameters on the microstructural characteristics and mechanical properties of the dissimilar joint between 17-4PH precipitation hardening stainless steel and Ti6Al4V alloy. For this purpose, the welding of these two alloys was done without an interlayer and with an interlayer of copper with a thickness of 0.8 mm. Two different...
متن کاملProduction of Fe-TiN and Fe-Ti(N,C) composite powders by mechanical alloying
In this research, the production of Fe-TiN and Fe-Ti(N,C) composite powders by mechanical alloying was investigated and evaluated. Ferrotitanium (containing 70%Ti), titanium and graphite were used as the raw materials. Initial mixtures were milled in different time durations under the pure nitrogen atmosphere with the pressure of 5atm. The results showed that when N2 pressure is 5 at...
متن کامل