چکیده
The effects of surfactant polyacrylate acid (PAA) on shape evolution of 0.7Pb(Mg1/3Nb2/3)O3-0.3PbTiO3 (0.7PMN-0.3PT) nanorods were studied. The results revealed that the polyacrylic acid content had great influence on the morphology of 0.7PMN-0.3PT. With increasing PAA concentration from 0.45 to 0.82 g/ml, the ratio of perovskite phase (PMN-PT nanorod) increased, while the ratio of pyrochlore phase decreased. When the PAA concentration was 0.82 g/ml, pure 0.7PMN-0.3PT nanorods were obtained. However, when PAA concentration was higher than 0.82 g/ml, the excess of PAA would hindered their [100] orientation growth. The piezoelectric coefficient d 33 of 0.7PMN-0.3PT nanorod was obtained by linear fitting, and the d 33 value was 409 pm/V.
منابع مشابه
High yield synthesis of catalytically active five-fold twinned Pt nanorods from a surfactant-ligated precursor.
The CO-assisted thermal decomposition of a new, surfactant-ligated Pt precursor, [Pt(acac)(NHR)](n) (n = 2, 3; R = C(18)H(37)), gives structurally uniform five-fold twinned Pt nanorods. The Pt nanorods, mostly covered by {100} facets, exhibit much enhanced electrocatalytic activity over {100} faceted Pt nanocubes, indicating the superior catalytic performance due to the presence of the reactive...
متن کاملPMN-PT/PVDF Nanocomposite for High Output Nanogenerator Applications
The 0.7Pb(Mg1/3Nb2/3)O₃-0.3PbTiO₃(0.7PMN-0.3PT) nanorods were obtained via hydrothermal method with high yield (over 78%). Then, new piezoelectric nanocomposites based on (1-x)Pb(Mg1/3Nb2/3)O₃-xPbTiO₃ (PMN-PT) nanorods were fabricated by dispersing the 0.7PMN-0.3PT nanorods into piezoelectric poly(vinylidene fluoride) (PVDF) polymer. The mechanical behaviors of the nanocomposites were investiga...
متن کاملSurfactant-assisted synthesis of Barium hexaferrite nanoparticles by hydrothermal method
In the present work, the synthesis of Barium hexaferrite (BaFe12O19) nanoparticles in thepresence of a large excess amount of OH− anions by the hydrothermal method in the presence and absence of surfactants such as Sodium dodecyl benzene sulfonate and Triton X-114 was reported. The optimized temperature in the absence of surfactant was determined (200 °C) and then Barium hexaferrite nanoparticl...
متن کاملSurfactant-free hydrothermal synthesis of lithium aluminate microbricks and nanorods from aluminium oxide nanoparticles.
Beta-LiAlO2 microbricks and rectangular nanorods have been successfully synthesized from Al2O3 nanoparticles by a simple hydrothermal process without any surfactant or template, by simply changing the Li/Al molar ratio.
متن کاملMicrowave-assisted rapid synthesis of Co3O4 nanorods from CoC2O4.2H2O nanorods and its application in photocatalytic degradation of methylene blue under visible light irradiation
In this work, Co3O4 nanorods were successfully prepared by microwave-assisted solid state decomposition of rod-like CoC2O4.2H2O precursor within a very short reaction time (6 min) without the use of a solvent/surfactant and complicated equipment. The as-obtained Co3O4 nanorods were fully characterized by X-ray diffract...
متن کامل