The effect of cyclic martensitic transformations on diffusion of cobalt atoms in Fe-18wt.%Mn-2wt.%Si alloy
نویسندگان
چکیده
Diffusion characteristics of cobalt atoms were investigated using radioactive isotope method in phase-hardened Fe-18wt.%Mn-2wt.%Si alloy. The observed significant increase of diffusion coefficient of cobalt atoms under the cyclic γ-ε-γ martensitic transformations was due to the action of two independent mechanisms - an athermal one and a thermally activated one. The first one arose from the direct γ-ε and the reverse ε-γ transformations with corresponding direct and reverse lattice shears during alternating stresses and simultaneous lattice restructuring. Another mechanism arose under the diffusion annealing of the phase-hardened alloy.
منابع مشابه
Cyclic Martensitic Transformations Influence on the Diffusion Of Carbon Atoms in Fe-18 wt.%Mn-2 wt.%Si alloy
A significant carbon diffusion mobility acceleration as a result of cyclic γ↔ε martensitic transformations in iron-manganese alloy is determined by one- and two-dimensional structure defects of ε-martensite with face-centered close-packed lattice. Such defects (dislocations, low angle sub-boundaries of dislocations, chaotic stacking faults) were formed during cyclic γ↔ε martensitic transformati...
متن کاملThe Formation of Crystal Defects in a Fe-Mn-Si Alloy Under Cyclic Martensitic Transformations.
Formation of crystalline defects due to cyclic martensitic transformations (CMT) in the iron-manganese Fe-18 wt.% Mn-2 wt.% Si alloy was investigated using X-ray diffractometry. Conditions for accumulation of fragment sub-boundaries with low-angle misorientations and chaotic stacking faults in crystal lattice of austenite and ε-martensite were analyzed.
متن کاملThe effect of multiple martensitic transformations on diffusion of Fe and Ni atoms in Fe-31.7%Ni-0.06%C alloy
Diffusion characteristics of iron and nickel atoms were investigated using radioactive isotopes method in phase-hardened metastable iron-nickel Fe-31.7%Ni-0.06%C alloy with nanofragmented structure. It has been found that diffusion mobility of nickel and iron atoms in reverted austenite of Fe-31.7%Ni-0.06%C alloy significantly increases as the result of multiple γ-α-γ martensitic transformation...
متن کاملNanostructurization of Fe-Ni Alloy
Data about an effect of cyclic γ-α-γ martensitic transformations on the structure state of reverted austenite Fe-31.7 wt.% Ni-0.06 wt.% C alloy are presented. The effect of multiple direct γ-α and reverse α-γ martensitic transformations on fragmentation of austenitic grains has been investigated by electron microscopy and X-ray diffraction methods. An ultrafine structure has been formed by nano...
متن کاملEffect of Amount of Deformation on the Martensitic Transformation and Shape Memory Effect in Fe-Mn-Si based Shape Memory Steel
The effect of amount of deformation on the martensitic transformation and shape memory effect in a Fe-16Mn-5Si-9Cr-4Ni alloy is studied. It is found that both 6and a'martensite are induced by deformation. With increasing amount of deformation, y+~-nx' transformation is greatly enhanced. the highest shape memory strain 3 3% is reached when the amount of deformation is about 5%.