Evolution of Helium Bubbles and Discs in Irradiated 6H-SiC during Post-Implantation Annealing
نویسندگان
چکیده
The single crystal 6H-SiC with [0001] crystal direction irradiated by 400 keV He⁺ ions with 1 × 1017 ions/cm² fluence at 400 °C were annealed at 600, 900, 1200 and 1400 °C for different durations. The evolution of helium bubbles and discs was investigated by transmission electron microscopy. An irradiated layer distributed with fine helium bubbles was formed with a width of ~170 nm after helium ion irradiation. The size of gas bubbles increased with increasing annealing time and temperature and finally reached stable values at a given annealing temperature. According to the relationship between the bubble radii and annealing time, an empirical formula for calculating the bubble radii at the annealing temperature ranged from 600 to 1400 °C was given by fitting the experiment data. Planar bubble clusters (discs) were found to form on (0001) crystal plane at both sides of the bubble layer when the annealing temperature was at the range of 800-1200 °C. The mechanism of bubble growth during post-implantation annealing and the formation of bubble discs were also analyzed and discussed.
منابع مشابه
Investigation of Surface Morphology of 6H-SiC Irradiated with He+ and H2+ Ions
Light ion implantation is one of the important procedures of smart cut for SiC-based semiconductor fabrication. This work investigated the surface morphologies and microstructures of single crystal 6H-SiC irradiated by one or both of H₂⁺ and He⁺ ions at room temperature and then annealed at specific temperatures. Blisters evolved from the coalescence of H nanocracks were formed in the H₂⁺ and H...
متن کاملMicrostructural evolution of helium-implanted a-SiC
Helium has a decisive effect on the microstructure of silicon carbide materials after implantation and subsequent annealing. A dense population of bubbles and dislocation loops is already observed at relatively low displacement doses after annealing of helium-implanted a-SiC, while no visible damage appears after irradiation without helium implantation under otherwise equal conditions. The defe...
متن کاملIn situ Observation of Microstructure Evolution in 4H-SiC under 3.5keV He Irradiation
4H-SiC was irradiated with 3.5 keV He ions using the MIAMI facility at University of Huddersfield. The evolution of microstructure and gas bubbles during the irradiation at 700°C, 800°C and 900°C was observed by in situ transmission electron microscopy. Under irradiation, isolated bubbles and bubble discs formed in the SiC matrix. Bubble discs lying on {0001} and {10-10} crystal planes were beg...
متن کاملRecrystallization-Induced Surface Cracks of Carbon Ions Irradiated 6H-SiC after Annealing
Single crystal 6H-SiC wafers with 4° off-axis [0001] orientation were irradiated with carbon ions and then annealed at 900 °C for different time periods. The microstructure and surface morphology of these samples were investigated by grazing incidence X-ray diffraction (GIXRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). Ion irradiation induced SiC amorphizat...
متن کاملEffect of Annealing on Microstructures and Hardening of Helium-Hydrogen-Implanted Sequentially Vanadium Alloys
The effect of post-irradiation annealing on the microstructures and mechanical properties of V-4Cr-4Ti alloys was studied. Helium-hydrogen-irradiated sequentially V-4Cr-4Ti alloys at room temperature (RT) were undergone post-irradiation annealing at 450 °C over periods of up to 30 h. These samples were carried out by high-resolution transmission electron microscopy (HRTEM) observation and nanoi...
متن کامل