Design and fabrication of compositionally graded inorganic oxide thin films: Mechanical, optical and permeation characteristics

نویسندگان

  • Y.-H. Choi
  • X. Bulliard
  • A. Benayad
  • D. Choi
چکیده

Different types of inorganic oxide films composed of a chemical composition gradient single layer were designed, fabricated and characterized. Compositionally graded thin films were created by power-controlled co-sputtering of alumina (Al2O3) and silica (SiO2) at room temperature, allowing the structural design of the film to be tailored at the nanometer scale. Two distinct graded thin films were fabricated: one with a compositionally asymmetric structure consisting of a SiO2-rich bottom interface and a Al2O3-rich top surface, and the other with a compositionally balanced sandwich structure consisting of both the top surface and bottom interface rich in SiO2 and a core rich in Al2O3 (referred to as SGS for ‘sandwich graded structure’). Smoothly graded thin films without interfacial boundaries were verified by Auger electron spectroscopy profiles. X-ray photoelectron spectroscopy demonstrated that the Al2O3/SiO2 graded structures consisted of Si–O and Al–O bonds, as well as Al–O–Si bonds in the transition layer. Neat Al2O3 or SiO2 and their graded ones were all investigated for their mechanical, optical and permeation properties. A SGS thin film presented the best mechanical stability (i.e., about three times improved film toughness of a neat Al2O3 single layer), demonstrating that balanced internal stresses and alternating bonding structures, achieved via a graded structure without interfaces, are crucial for enhancing mechanical stability. Furthermore, neat and graded thin films exhibited the similar level of optical transmittance and the permeation properties for the graded films were well matched with the behaviors of mechanical stability. 2010 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

برای دانلود رایگان متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Fabrication of Graphene Oxide Thin Films on Transparent Substrate via a Low-Voltage Electrodeposion Technique

Graphene oxide (GO) thin films were simply deposited on fluorine doped tin oxide (FTO) substrate via a low-voltage electrodeposition. The GO and GO thin films were characterized by Zeta Potential, X-ray diffraction, Ultraviolet-Visible spectroscopy, atomic force microscopy, Fourier transform infrared spectroscopy, field emission scanning electron microscopy and energy dispersive X-ray spectrosc...

متن کامل

Structural, Electrical and Optical Properties of Molybdenum Oxide Thin Films Prepared by Post-annealing of Mo Thin Films

Molybdenum thin films with 50 and 150 nm thicknesses were deposited on silicon substrates, using DC magnetron sputtering system, then post-annealed at different temperatures (200, 325, 450, 575 and 700°C) with flow oxygen at 200 sccm (standard Cubic centimeter per minute). The crystallographic structure of the films was obtained by means of x-ray diffraction (XRD) analysis. An atomic force micr...

متن کامل

Structural, Electrical and Optical Properties of Molybdenum Oxide Thin Films Prepared by Post-annealing of Mo Thin Films

Molybdenum thin films with 50 and 150 nm thicknesses were deposited on silicon substrates, using DC magnetron sputtering system, then post-annealed at different temperatures (200, 325, 450, 575 and 700°C) with flow oxygen at 200 sccm (standard Cubic centimeter per minute). The crystallographic structure of the films was obtained by means of x-ray diffraction (XRD) analysis. An atomic force micr...

متن کامل

Ultraviolet detectors based on annealed zinc oxide thin films: epitaxial growth and physical characterizations

In this report, ultraviolet (UV) detectors were fabricated based on zinc oxide thin films. The epitaxial growth of zinc oxide thin films was carried out on bare glass substrate with preferred orientation to (002) plane of wurtzite structure through radio frequency sputtering technique. The structural properties indicated a dominant peak at 2θ=34.28º which was matched with JCPDS reference card N...

متن کامل

A Study of ZnO Buffer Layer Effect on Physical Properties of ITO Thin Films Deposited on Different Substrates

The improvement of the physical properties of Indium Tin Oxide (ITO) layers is quite advantageous in photovoltaic applications. In this study the ITO film is deposited by RF sputtering onto p-type crystalline silicon (c-Si) with (100) orientation, multicrystalline silicon (mc-Si), and glass substrates coated with ZnO and annealed in vacuum furnace at 400°C. Electrical, optical, structural a...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2010