Hydrogen Induced Abrupt Structural Expansion at High Temperatures of a Ni32Nb28Zr30Cu10 Membrane for H2 Purification
نویسندگان
چکیده
Ni-Nb-Zr amorphous membranes, prepared by melt-spinning, show great potential for replacing crystalline Pd-based materials in the field of hydrogen purification to an ultrapure grade (>99.999%). In this study, we investigate the temperature evolution of the structure of an amorphous ribbon with the composition Ni32Nb28Zr30Cu10 (expressed in atom %) by means of XRD and DTA measurements. An abrupt structural expansion is induced between 240 and 300 °C by hydrogenation. This structural modification deeply modifies the hydrogen sorption properties of the membrane, which indeed shows a strong reduction of the hydrogen capacity above 270 °C.
منابع مشابه
Preparation of Pd composite membrane via organic-inorganic activation method in electroless plating technique
A palladium composite membrane was prepared via electroless plating technique using organic-inorganic method during activation process. The ceramic support surface was modified by two TiO2-boehmite and one γ-alumina layers to avoid Pd penetration in support pores. Thin and defect-free Pd composite membrane was obtained by creating a relative smoothness on the ceramic support and using Pd nanopa...
متن کاملEffect of Dehydration Temperature on the H2 Separation Potential of Hydroxy Sodalite Zeolite Membranes
The main goal of this work was to synthesize and evaluate the effect of dehydration temperature on the potential application of hydroxy sodalite zeolite membrane. Hydroxy sodalite zeolite membranes were synthesized via direct hydrothermal method onto a tubular alumina support without seeding in a hot air oven. The synthesized membranes were characterized by X-ray diffraction (XRD) and scanning ...
متن کاملDevelopment of Palladium-Alloy Membranes for Hydrogen Separation and Purification
This paper summarizes R&D activities and progress at NORAM Engineering and the University of British Columbia (UBC) on preparation and testing of thin palladium-based membranes and their applications. Most of these activities were carried out internally at NORAM, some jointly with UBC and their spin-off company, Membrane Reactor Technology (MRT) through a wide range of projects. Key results out...
متن کاملSynthesis of a Multilayer Ceramic Membrane Used for Hydrogen Separation at High Temperature
A multilayer composite ceramic membrane was prepared by depositing a nano-scale layer of SiO2 on top of a modified porous alumina support by chemical vapor deposition (CVD) method. The modification of the support was carried out by adding a graded layer of Al2O3 (γ-alumina phase), using sol-gel method. An optimized temperature of 700 K for intermediate layer calcination was gained by XRD analys...
متن کاملPreparation of BaCe0.9Yb0.1O3-δ asymmetrical membrane for hydrogen separation at high tempratures
A mixed proton–electron conducting perovskite was synthesized by liquid-citrate method and the corresponding membrane was prepared by pressing followed by sintering. The hydrogen permeability of BaCe0.9Yb0.1O3-δ was studied as a function of temperature and hydrogen partial pressure (PH2) gradient. Using 100% dry hydrogen at 1173 K, the hydrogen permeation rate of dense membranes (1.63 mm thick)...
متن کامل