Size-selected growth of transparent well-aligned ZnO nanowire arrays
نویسندگان
چکیده
This paper reports the effect of precursor concentration, growth temperature, and growth time on the size and density of ZnO nanowire arrays (ZNAs). The well-aligned ZNAs were grown on indium tin oxide substrate using a facile chemical bath deposition method. The results showed that the ZnO nanowires could be tailored to the desired sizes with a simple variation of the growth parameters. Optical transmission spectra revealed a sufficient transparency of the ZNAs, qualifying them for photovoltaic and other optoelectronic applications. An inverted hybrid solar cell was fabricated using the ZNAs as the electron collecting layer, and the solar cell exhibited a power conversion efficiency of 0.91%.
منابع مشابه
Patterned growth of vertically aligned ZnO nanowire arrays on inorganic substrates at low temperature without catalyst.
We report an approach for growing aligned ZnO nanowire arrays with a high degree control over size, orientation, dimensionality, uniformity, and possibly shape. Our method combines e-beam lithography and a low temperature hydrothermal method to achieve patterned and aligned growth of ZnO NWs at <100degreesC on general inorganic substrates, such as Si and GaN, without using catalyst. This approa...
متن کاملGrowth and characterization of ZnO/ZnTe core/shell nanowire arrays on transparent conducting oxide glass substrates
We report the growth and characterization of ZnO/ZnTe core/shell nanowire arrays on indium tin oxide. Coating of the ZnTe layer on well-aligned vertical ZnO nanowires has been demonstrated by scanning electron microscope, tunneling electron microscope, X-ray diffraction pattern, photoluminescence, and transmission studies. The ZnO/ZnTe core/shell nanowire arrays were then used as the active lay...
متن کاملDiameter-Controlled Vapor-Solid Epitaxial Growth and Properties of Aligned ZnO Nanowire Arrays
A facile, template-free method was used to grow large areas of well-aligned ZnO nanowire arrays on amorphous SiO2 substrates. The arrays are composed of vertically aligned, single-crystalline, wurtzitic [001] ZnO nanowires whose diameters were easily controlled by growth temperature, adjusted by changing the distance between the substrate and the precursor material in the growth chamber. A vapo...
متن کاملGrowth of ZnO nanowires on retroreflector microspheres and the resulting light channeling and plasmonic properties
We have investigated the growth of ZnO nanowires on curved BaTi03 retroreflector beads, as well as grov.1h of ZnO nanowires on flat substrates. Results indicate that the growth of ZnO aligned nanowire arrays occurs farther away from the Zn source in the retroreflectors, while the results are opposite for the flat Si substrates. In the case of the ZnO nanowires on flat Si, the nanowires formed i...
متن کاملControllable synthesis of branched ZnO/Si nanowire arrays with hierarchical structure
A rational approach for creating branched ZnO/Si nanowire arrays with hierarchical structure was developed based on a combination of three simple and cost-effective synthesis pathways. The crucial procedure included growth of crystalline Si nanowire arrays as backbones by chemical etching of Si substrates, deposition of ZnO thin film as a seed layer by magnetron sputtering, and fabrication of Z...
متن کامل