Magnetic Properties of Y3−2xCa2xFe5−xVxO12 Garnets
نویسندگان
چکیده
A comprehensive study of the magnetic properties of Y3−2xCa2xFe5−xVxO12 (0 ≤ x ≤ 1) has been performed. The garnet ferrites samples were prepared by the ceramic technique, and X-ray diffraction analysis indicates the formation of single cubic phase. Vibrating sample magnetometry (VSM) and a superconducting quantum-interference device (SQUID) were used to measure the magnetic properties, especially the magnetization and thermo-magnetic behavior. The magnetization curves exhibit the typical characteristics of ferrimagnetic materials at both 4.2 K and at room temperature. The samples have a low coercivities (between 20 and 40 Oe) and saturation magnetizations as high as 36 emu/g at 4.2 K. The saturation magnetization decreases with V and Ca contents, reaching about 8 emu/g at 4.2 K (x = 1). For all samples, the saturation magnetization decreases with increasing temperature, whereas the Curie temperature increases for small values of x, from 557 K for x = 0 to a maximum of 590 K for x = 0.2. For larger values of x, it decreases and reaches 525 K for x = 1.0. The basic experimental trends reflect the occupancy of the tetrahedral 24d sites by vanadium in combination with the predominant intersublattice exchange constant Jad, although the nonzero magnetization at x = 1.0 indicates that about 10% of the substituted V atoms goes onto the octahedral 16a sites.
منابع مشابه
Structure and Magnetic Properties of Polycrystalline Y3-xLaxFe5O12 Garnets
L a substituted polycrystalline Y,.,LaXFe5C),2 (x 0.0 0.5) garnets were manufactured by ceramic method and the structure and magnetic properties of the garnets were studied by X-ray diffractometry, magnetometry , ferromagnetic resonance and permittivity and permeability measurement. Saturation magnetization and Curie temperature of the garnets increase slightly with increasing La content. Reson...
متن کاملبررسی ویژگیهای مغناطیسی و بیناب سنجی موسبائر ذرات گارنت ایتریوم آهن بیسموتی Y3-xBixFe5O12 تهیه شده به روش سل-ژل
In this research, Y3-xBixFe5O12 x = (0, 0.1, 0.2, 0.3) were synthesized by a sol–gel method. X-ray diffraction (XRD) patterns confirmed the pure spinel structure for all samples. The magnetic properties of the samples were investigated by the vibration sample magnetometer (VSM). The results obtained from VSM showed that saturation magnetization increases up to x = 0.1 and then decreases for x>...
متن کاملLuminescence Properties of Oxyfluoride Glass and Glass Ceramic Doped with Y3 + Ions
Oxyfluoride glass ceramics containing CaF2nano-crystals doped with Y3+ ions were prepared by one-step crystallization of SiO2- Al2O3- CaO- CaF2 glasses at different temperatures. X- ray diffraction (XRD) results have revealed that CaF2 was the only precipitated crystalline phase in glass ceramic samples. According to the XRD results, a glass ceramic was selected as the best sample in order to ...
متن کاملTemperature Evolution of the Double Umbrella Magnetic Structure in Terbium Iron Garnet
The rare earth iron garnets RE3Fe5O12 (REIG hereafter) have been discovered at Grenoble (France) (Bertaut & Forrat, 1956; Bertaut et al., 1956) then independently at Murray Hill (USA) (Geller & Gilleo, 1957a, 1957b). These most studied ferrimagnetic materials have a general formula {RE3+3}[Fe3+2](Fe3+3)O12 where RE3+ can be any trivalent rare earth ion or the Yttrium Y3+. The crystal structure ...
متن کاملTitle : Development of Magnetic Field Sensors Using Bismuth – Substituted Garnets Thin Films with In - Plane Magnetization
Dissertation Title : Development of Magnetic Field Sensors Using Bismuth – Substituted Garnets Thin Films with In-Plane Magnetization Iulian Nistor, Ph.D., 2006 Dissertation Directed By: Professor of Engineering Isaak D. Mayergoyz, Electrical and Computer Engineering Department, and Dr. Charles Krafft, Laboratory for Physical Sciences In the dissertation, the use of magnetic single crystal Bism...
متن کامل