Graphene reinforced biodegradable poly(3-hydroxybutyrate-co-4-hydroxybutyrate) nano-composites
نویسندگان
چکیده
Novel biodegradable poly(3-hydroxybutyrate-co-4-hydroxybutyrate) [PHBV]/graphene nanocomposites were prepared by solution casting. The thermal properties, crystallization behavior, microstructure, and fracture morphology of the composites were investigated. Scanning electron microscope (SEM) results show that graphene layers are homogeneously dispersed in the polymer matrix. X-ray diffraction (XRD) and dynamic scanning calorimetry (DSC) studies show that the well dispersed graphene sheets act as nucleating agent for crystallization. Consequently, the mechanical properties of the composites have been substantially improved as evident from dynamic mechanical and static tensile tests. Differential thermal analysis (DTA) showed an increase in temperature of maximum degradation. Soil degradation tests of PHBV/graphene nanocomposites showed that presence of graphene doesn’t interfere in its biodegradability.
منابع مشابه
Production and characterization of biodegradable terpolymer poly(3-hydroxybutyrate-co-3-hydroxyvalerate-co-4-hydroxybutyrate) by Alcaligenes sp. A-04.
The production of the terpolymer poly(3-hydroxybutyrate-co-3-hydroxyvalerate-co-4-hydroxybutyrate), P(3HB-co-3HV-co-4HB), by Alcaligenes sp. A-04 was investigated to determine the superior biodegradable polymer properties over those of poly(3-hydroxybutyrate), P(3HB), and its copolymers. The highest terpolymer content of 68% (w/w) was produced by Alcaligenes sp. A-04 at 60 h by shake-flask cult...
متن کاملPoly(3-hydroxybutyrate-co-3-hydroxyvalerate) composite biomaterials for bone tissue regeneration: in vitro performance assessed by osteoblast proliferation, osteoclast adhesion and resorption, and macrophage proinflammatory response.
The efficacy of composite materials for bone tissue engineering is dependent on the materials' ability to support bone regeneration whilst inducing a minimal inflammatory response. In this study we examined the in vitro osteogenic and inflammatory properties of poly(3-hydroxybutyrate-co-3-valerate) (PHBV) with various calcium phosphate-reinforcing phases: nano-sized hydroxyapatite (HA); submicr...
متن کاملProduction of poly(3-hydroxybutyrate-co-4-hydroxybutyrate) in recombinant Escherichia coli grown on glucose.
A recombinant Escherichia coli strain has been developed that produces poly(3-hydroxybutyrate-co-4-hydroxybutyrate) when grown in complex medium containing glucose. This has been accomplished by introducing into E. coli DH5 alpha separate plasmids harboring the polyhydroxyalkanoate (PHA) biosynthesis genes from Ralstonia eutropha (formerly named Alcaligenes eutrophus) and the succinate degradat...
متن کاملSingle crystal morphologies of biodegradable aliphatic polyesters
Single crystals of biodegradable aliphatic polyesters, poly([R]-3-hydroxybutyrate), poly([R]-3-hydroxyvalerate), poly(L-lactic acid), poly( -propiolactone), poly(4-hydroxybutyrate), poly(Æ-valerolactone), poly("caprolactone), poly(ethylene succinate) and poly(tetramethylene adipate), were grown from dilute solution by isothermal crystallization, and the crystal structures and morphologies were ...
متن کاملApplication of the Taguchi Design for Production of Poly(β-hydroxybutyrate) by Ralstonia eutropha
The Taguchi design of experiments was used to test the relative importance of medium components and environmental factors on poly(β-hydroxybutyrate)(PHB) production by Ralstonia eutropha. The optimum condition was obtained as: fructose concentration, 15 g/L; C/N ratio, 7.4; agitation speed 200 rpm; culture time, 40 h; temperature, 25 ° C; seed age, 15 h. At optimu...
متن کامل