Enhancement of Mechanical and Thermal Properties of Polycaprolactone/Chitosan Blend by Calcium Carbonate Nanoparticles
نویسندگان
چکیده
This study investigates the effects of calcium carbonate (CaCO(3)) nanoparticles on the mechanical and thermal properties and surface morphology of polycaprolactone (PCL)/chitosan nanocomposites. The nanocomposites of PCL/chitosan/CaCO(3) were prepared using a melt blending technique. Transmission electron microscopy (TEM) results indicate the average size of nanoparticles to be approximately 62 nm. Tensile measurement results show an increase in the tensile modulus with CaCO(3) nanoparticle loading. Tensile strength and elongation at break show gradual improvement with the addition of up to 1 wt% of nano-sized CaCO(3). Decreasing performance of these properties is observed for loading of more than 1 wt% of nano-sized CaCO(3). The thermal stability was best enhanced at 1 wt% of CaCO(3) nanoparticle loading. The fractured surface morphology of the PCL/chitosan blend becomes more stretched and homogeneous in PCL/chitosan/CaCO(3) nanocomposite. TEM micrograph displays good dispersion of CaCO(3) at lower nanoparticle loading within the matrix.
منابع مشابه
Biodegradable kefiran-chitosan-nanocellulose blend film: Production and physical, barrier, mechanical, thermal, and structural properties
In this study, biodegradable kefiran-chitosan-nanocellulose blend films were developed and their physical, mechanical, barrier, thermal and structural properties determined. Results showed that adding nanocellulose had not any significant effect on the thickness, moisture content and water solubility. Also, water vapor permeability, tensile strength and lightness increased and the elongation at...
متن کاملBiological Properties of Blend Nanofibrous Scaffolds from Poly(caprolactone)-Chitosan-Poly(vinyl alcohol)
متن کامل
Effect of Alumina Nanoparticles on the Enhancement of Shape Memory, Mechanical and Impact Properties of TPU/ABS blend
In this paper, the shape memory, mechanical and Izod impact properties of a new shape memory nanocomposite based on thermoplastic polyurethane (TPU), acrylonitrile butadiene styrene (ABS) and alumina nanoparticles were investigated. The morphological results showed that the presence of 1% alumina nanoparticles made a reduction in diameter of ABS domains and caused a uniform distribution of the ...
متن کاملRole of Nano-Sized TiO2 on Mechanical and Thermal Behavior of Starch/Poly (vinyl alcohol) Blend Films
A novel Starch/Poly (vinyl alcohol)/nano-Titanium dioxide (ST/PVA/nano-TiO2) biodegradable nanocomposite film was prepared by homogeneously dispersed TiO2 nanoparticles in different ratios of starch/PVA-based materials, via a solution casting method. Glycerol was used as plasticizer. The mechanical and thermal properties of films were studied using tensile and perforation strength tests and the...
متن کاملPreparation and Properties of Polycaprolactone/Poly (Butylene Terephthalate) Blend
Polycaprolactone (PCL) and poly(butylene terephthalate) (PBT) blend was prepared by melt processing. The PCL/PBT blend showed similar morphology with that of pure PCL.The crystallization temperature of PCL was increased by the incorporation of PBT. It was also observed that the peak height in the DSC thermograms decreased and then disappeared by adding 40 % or more PBT which might be due to...
متن کامل