ÐOngoing research is reported aimed at improving bio®xation through the use of bioactive glass coatings on Ti-based implant alloys. The optimized processing conditions for coating with one promising bioactive glass composition are discussed, and the stress corrosion crack growth behavior in a simulated human physiological environment is presented. This glass can be successfully used to coat Ti implant alloys, and preliminary tests indicate that interfacial fracture resistance is good. # 1999 Acta Metallurgica Inc. Published by Elsevier Science Ltd. All rights reserved.
منابع مشابه
Pii: S1359-6454(99)00264-5
ÐThe grain boundary segregation of Bi in dilute polycrystalline Cu±Bi alloys was systematically studied as a function of temperature and composition. The temperature dependencies of the Gibbsian excess of Bi at the grain boundaries exhibited discontinuous changes at the temperatures close to, but dierent from the bulk solidus temperatures. The observed segregational phase transition was interp...
متن کاملPii: S1359-6454(99)00023-3
ÐThe durability of residually compressed coatings, particularly thermal barrier coatings (TBCs), is governed by events occurring at the interface with the substrate. In general, failure involves the sequential nucleation growth and coalescence of separations in the presence of imperfections and defects. The growth and coalescence phases are analyzed. Remnant ligaments are expected from the mech...
متن کاملPii: S1359-6454(99)00156-1
ÐThe eect of hydrogen in solid solution on the edge/screw character of dislocations has been investigated by deforming samples of high-purity aluminum in a gaseous hydrogen environment in situ in a controlled environment transmission electron microscope. Solute hydrogen was found to stabilize edge segments of dislocations, which inhibited, and in some cases stopped dislocations from cross-slip...
متن کاملPii: S1359-6454(96)00395-3
Debonding of films attached to substrates as well as fibers embedded in matrices typically involves initiation, steady-state propagation and a final transient as the debond converges on an edge or another debond. The emphasis in this paper is on the mechanics of the transient. Under most circumstances, a converging debond crack is characterized by an energy release rate that approaches zero, ca...
متن کاملPii: S1359-6454(99)00214-1
ÐSamples of superelastic NiTi and superelastic NiTi reinforced with 10 vol.% TiC particles were deformed under uniaxial compression to 975 MPa while neutron diraction spectra were simultaneously collected. Despite the presence of sti TiC particles, a macroscopic strain of 3% was obtained in the composite on loading and was fully recovered on unloading. The diraction spectra were analyzed by ...