Radio Frequency Coplanar ZnO Schottky Nanodiodes Processed from Solution on Plastic Substrates.
نویسندگان
چکیده
Coplanar radio frequency Schottky diodes based on solution-processed C60 and ZnO semiconductors are fabricated via adhesion-lithography. The development of a unique asymmetric nanogap electrode architecture results in devices with a high current rectification ratio (10(3) -10(6) ), low operating voltage (<3 V), and cut-off frequencies of >400 MHz. Device fabrication is scalable and can be performed at low temperatures even on plastic substrates with very high yield.
منابع مشابه
Effect Of Zinc Oxide RF Sputtering Pressure on the Structural and Optical Properties of ZnO/PEDOT:PSS Inorganic/Organic Heterojunction
Zinc oxide nanostructures are deposited on glass substrates in the presenceof oxygen reactive gas at room temperature using the radio frequency magnetronsputtering technique. In this research, the effects of zinc oxide sputtering pressure on thenanostructure properties of the deposited layer are investigated. The deposition pressurevaries from 7.5 to 20.5 mTorr. AFM resu...
متن کاملMorphological, structural and photoresponse characterization of ZnO nanostructure films deposited on plasma etched silicon substrates
ZnO nanostructure films were deposited by radio frequency (RF) magnetron sputtering on etched silicon (100) substrates using dry Ar/SF6 plasma, at two etching times of 5 min and 30 min, and on non etched silicon surface. Energy dispersive X-ray (EDX) technique was employed to investigate the elements contents for etched substrates as well as ZnO films, where it is found to be stoichiometric. Su...
متن کاملNanowire Piezoelectric Nanogenerators on Plastic Substrates as Flexible Power Sources for Nanodevices
Research applications in biomedical science and technology usually require various portable, wearable, easy-to-use, and/or implantable devices that can interface with biological systems. Organic or hybrid organic–inorganic microelectronics and nanoelectronics have long been a possibility. However, these devices require a power source, such as electrochemical cells or piezoelectric, thermoelectr...
متن کاملDual-Gate ZnO Thin-Film Transistors with SiNx as Dielectric Layer
We report on the fabrication of coplanar dual-gate ZnO thin-film transistors with 200-nm thickness SiNx for both top and bottom dielectrics. The ZnO film was deposited by RF magnetron sputtering on SiO2/Si substrates at 100◦C. And the thickness of ZnO film is compared with 100-nm and 40-nm. This TFT has a channel width of 100-μm and channel length of 5-μm. The fabricated coplanar dual-gate ZnO ...
متن کاملEnhanced Physical Properties Of Indium Tin Oxide Films Grown on Zinc Oxide-Coated Substrates
Structural, electrical and optical properties of indium tin oxide or ITO (In2O3:SnO2) thin films on different substrates are investigated. A 100-nm-thick pre-deposited zinc oxide (ZnO) buffer layer is utilized to simultaneously improve the electrical and optical properties of ITO films. High purity ZnO and ITO layers are deposited with a radio frequency sputtering in argon ambient with plasma p...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
- Small
دوره 12 15 شماره
صفحات -
تاریخ انتشار 2016