Strain Rate Sensitivity Studies of Cryomilled Al Alloy Performed by Nanoindentation
نویسندگان
چکیده
Al 5083 alloy powder was mechanically milled in liquid nitrogen to achieve a nanocrystalline (NC) structure having an average grain size of 50 nm with high thermal stability, and then consolidated by quasi-isostatic (QI) forging. The consolidation resulted in ultrafine grains (UFG) of about 250 nm, and the bulk material exhibited enhanced strength compared to conventionally processed Al 5083. The hardness of as-cryomilled powder and the UFG material was measured by nanoindentation using loading rates in the range of 50−50,000 μN/s, and results were compared with the conventional grain size alloy. Negative strain rate sensitivity was observed in the cryomilled NC powder and the forged UFG plate, while the conventional alloy was relatively strain rate insensitive.
منابع مشابه
Effect of grain size on strain rate sensitivity of cryomilled Al– Mg alloy
Al–Mg alloy powder was cryomilled to achieve a nanocrystalline (NC) structure having an average grain size of 50 nm with high thermal stability, and then consolidated by quasi-isostatic forging. The consolidation resulted in a bulk material with ultrafine grains of about 250 nm, and the material exhibited enhanced strength compared to conventionally processed Al–Mg alloy. The hardness of as-cry...
متن کاملSelf-annealing in a two-phase Pb-Sn alloy after processing by high-pressure torsion
A Pb-62% Sn two-phase eutectic alloy was processed by high-pressure torsion (HPT) and stored at room temperature (RT) to investigate the occurrence of self-annealing. The microstructural characteristics and mechanical properties were recorded during self-annealing using scanning electron microscopy, tensile testing and nanoindentation. Processing by HPT produces a weakening effect but storage a...
متن کاملThe effect of temperature and strain rate on elongation to failure in nanostructured Al-0.2wt% Zr alloy fabricated by ARB process
A nano/ultra-fine grain Al-0.2wt% Zr alloy was produced by accumulated roll bonding (ARB) processafter 10 cycles. The fraction of high angle grain boundaries increased from 8% to 65.4% during 10passes during ARB process. This alloy was subjected to tensile test at different temperatures (523,573and 623 K) and strain rates (0.1 and 0.01 s-1). The optimum condition of temperature and strain rate ...
متن کاملEffect of strain rate on the formation of nanocrystallites in an Al-based amorphous alloy during nanoindentation
The effect of deformation by nanoindentation on nanocrystallization in amorphous Al90Fe5Gd5 was investigated by transmission electron microscopy. Massive precipitation of nanocrystallites is observed within the indents. Under the quasistatic condition used, a temperature rise due to adiabatic heating is likely negligible, confirming that plastic deformation can induce crystallization without a ...
متن کاملبررسی اثر اکستروژن در کانال زاویه دار همسان بر رفتار پیر کرنشی دینامیکی یک آلیاژ Al-Mg-Si-Cu
An Al-Mg-Si-Cu alloy was subjected to tensile testing, both under solutionized and ECAE-ed conditions, using strain rates of 10-4 s-1 to 10-1 s-1 at temperatures of 25 ˚C to 325 ˚C to investigate the dynamic strain aging (DSA) phenomenon in the alloy. Negative strain rate sensitivity (m) and increasing ultimate tensile stress were observed in the DSA region with increasing temperature . Regardi...