SELF-Cured Alkali Activated Slag Concrete Mixes- An Experimental Study
نویسنده
چکیده
Alkali Activated Slag Concrete (AASC) mixes are manufactured by activating ground granulated blast furnace slag (GGBFS) using sodium hydroxide and sodium silicate solutions. The aim of the present experimental research was to investigate the effect of increasing the dosages of sodium oxide (Na2O, in the range of 4 to 8%) and the activator modulus (Ms) (i.e. the SiO2/Na2O ratio, in the range of 0.5 to 1.5) of the alkaline solutions, on the workability and strength characteristics of self-cured (air-cured) alkali activated Indian slag concrete mixes. Further the split tensile and flexure strengths for optimal mixes were studied for each dosage of Na2O.It is observed that increase in Na2O concentration increases the compressive, split-tensile and flexural strengths, both at the early and later-ages, while increase in Ms, decreases the workability of the mixes. An optimal Ms of 1.25 is found at various Na2O dosages. No significant differences in the strength performances were observed between AASCs manufactured with alkali solutions prepared using either of potable and de-ionized water. Keywords—Alkali activated slag, self-curing, strength characteristics.
منابع مشابه
A Study of the Influence of Slag Alkali Level on the Alkali-Silica Reactivity of Slag Concrete
Ground granulated blast furnace slag (ggbs), can reduce the alkali load in concrete, despite its relatively high alkali content. Most research has been devoted to the efficacy of slag with an alkali content of less than 1.0% and this is reflected in guidance documents. A comparative assessment was made of the effect, if any, of the alkali level of ggbs on potential alkali-silica reactivity. Exp...
متن کاملEFFECTS OF SILICA MODULUS AND ALKALI CONCENTRATION ON ACTIVATION OF BLAST-FURNACE SLAG
Abstract: The use of alkali-activated cementitious materials especially over the past decades has significantly been increased. The goal of this research is to investigate the effects of silica modulus and alkali concentration on alkali-activation of blast-furnace slag. In this research, the most important physical characteristics of cementitious systems, i.e. the 28-day compressive strength...
متن کاملDurability Performance of Self Compacting Concrete Incorporating Alccofine and Fly Ash
The cost associated with the application of large volume of cement and synthetic admixtures was one of the major drawbacks of Self Compacting Concrete (SCC), which can be reduced by the use of supplementary cementitious materials (SCM). When the demand of cement reduces, the release of carbon dioxide (CO2) from cement industries will come down, which has a positive impact on global w...
متن کاملApplying Solid Residues of Copper Slag in Kerman Sarcheshme of Iran as Sand Replacement for Self-Compacting Concrete
The reuse of mineral wastes is one of the most suitable solid wastes solutions. Throughout the world, the large of the granular aggregates used in constructions exploit natural mountain resources and rivers. Using mineral waste as a part of concrete, it can be helped to create a green environment and also contribute to sustainable development. Since the copper production process in the Sarchesh...