In situ Transmission Electron Microscopy Studies of Electric-field-induced Phenomena in Ferroelectrics
نویسندگان
چکیده
High electric fields were delivered to specimens during imaging in the transmission electron microscopy (TEM) chamber to reveal details of electric field-induced phenomena in ferroelectric oxides. These include the polarization switching in nanometer-sized ferroelectric domains and the grain boundary cavitation in a commercial lead zirconate titanate (PZT) polycrystalline ceramic, the domain wall fracture in a Pb(Mg1/ 3Nb2/3)O3–PbTiO3 single crystal, and the transformation of incommensurate modulations in Pb0.99Nb0.02[(Zr1−xSnx)1−yTiy]0.98O3 (PZST100x/100y/2) polycrystalline ceramics. In the PZT ceramic, a cavitation process was uncovered for the electric field-induced intergranular fracture. In the ferroelectric single crystal, a preexisting crack was observed to deflect and to follow a 90° domain wall, indicating the presence of severe incompatible piezoelectric strains at thedomain wall. In the antiferroelectric PZST ceramics, the electric field-induced antiferroelectric-to-ferroelectric phase transformation was accompanied with the disappearance of incommensurate modulations.
منابع مشابه
Mechanical and Electrical Control of Charged Domain Walls in Ferroelectric Materials
Charged domain walls (CDWs) in ferroelectrics, as a result of “head-to-head” or “tail-to-tail” polarization configurations, are of significant scientific and technological importance, as they have been shown to play a critical role in affecting the atomic structures and controlling the electric, photoelectric and piezoelectric properties of ferroelectric materials. An understanding of the local...
متن کاملEx-situ studies on calcinations of structural, optical and morphological properties of post-growth nanoparticles CeO2 by HRTEM and SAED
Nanocrystalline particles of Cerium Oxide (CeO2) have been prepared by the chemical precipitation method using Cerium nitrate and Urea with a molar ratio of 1:2. The results revealed that the formation of CeO2 fine particles is influenced by molar ratio of metal nitrates to fuel. Well faceted CeO2 nanoparticles, were synthesized by thermal-assisted dissociation ...
متن کاملElectric-field-induced transformation of incommensurate modulations in antiferroelectric Pb0.99Nb0.02[(Zr1â‹TMxSnx)1â‹TMyTiy]0.98O3
Most antiferroelectric ceramics are modified from the prototype PbZrO3 by adding Sn and Ti in conjunction with small amount of Nb or La to optimize their properties. These modifiers introduce unique nanoscale structural feature to the ceramics in the form of incommensurate modulations. It was shown previously that the modulation is strongly responsive to a change in chemical composition or temp...
متن کاملEx-situ studies on calcinations of structural, optical and morphological properties of post-growth nanoparticles CeO2 by HRTEM and SAED
Nanocrystalline particles of Cerium Oxide (CeO2) have been prepared by the chemical precipitation method using Cerium nitrate and Urea with a molar ratio of 1:2. The results revealed that the formation of CeO2 fine particles is influenced by molar ratio of metal nitrates to fuel. Well faceted CeO2 nanoparticles, were synthesized by thermal-assisted dissociation ...
متن کاملDirect observations of electric field-induced domain boundary cracking in Š001‹ oriented piezoelectric Pb„Mg1Õ3Nb2Õ3...O3–PbTiO3 single crystal
In situ transmission electron microscopy study of electric field-induced cracking has been conducted on ^001& oriented 0.65Pb~Mg1/3Nb2/3!O3 – 0.35PbTiO3 crystal. Fracture of the 90° domain boundary was directly observed in the tetragonal area under both static and alternating electric fields. The field strength required to induce domain boundary cracking was lower for alternating electric field...