Unique magnetostriction of Fe68.8Pd31.2 attributable to twinning
نویسندگان
چکیده
Fe68.8Pd31.2 exhibits an anomalously large magnetostriction of ~400 ppm at room temperature as well as linear, isotropic, and hysteresis free magnetization behavior. This near perfectly reversible magnetic response is attributable to the presence of a large number of premartensitic magnetoelastic twin clusters present in the system made possible through the elastic softening that occurs near a martensitic transformation temperature of 252 K. It is proposed that the twin clusters in the material reduce both internal elastic and magnetic energy, causing the elastic and magnetic behavior of the material to be intimately linked. In such a framework, the anisotropy energy becomes extremely low causing the material to bear no crystalline dependence on magnetization, and application of a magnetic field causes simultaneous magnetic and twin domain movement which relaxes the system.
منابع مشابه
ناهمسانگردی چهتی مغناطوتنگش وگذارفاز مغناطیسی درمحلول جامدNd14 Dy2 Fe78 B6
In this research. The magnetic phase transition and anisotropic magnetoelastic effects of a polycrystalline sample of Nd14Dy2Fe78B6 were studied by susceptibility and magnetostriction measurements. The composition was prepared by casting method. SEM pictures and XRD analysis showed that it was composed of polycrystalline magnetic phases with the main phase of 2-14-1. Results of ac susceptibil...
متن کاملNanomechanical measurement of magnetostriction and magnetic anisotropy in (Ga,Mn)As.
A GaMnAs nanoelectromechanical resonator is used to obtain the first measurement of magnetostriction in a dilute magnetic semiconductor. Resonance frequency shifts induced by field-dependent magnetoelastic stress are used to simultaneously map the magnetostriction and magnetic anisotropy constants over a wide range of temperatures. Owing to the central role of carriers in controlling ferromagne...
متن کاملاثر جانشانی کبالت بر خواص مغناطوالاستیکی ترکیب Cu13Fe6Nd
In this research the magnetoelastic properties of Nd6Fe13-xCoxCu (x = 0 and 1) intermetallic compoundes are investigated. Analysis of X-ray diffraction patterns indicates that a single phase is formed approximately for x = 0 and the x = 1 sample is multi-phase. The lattice parameters were decreased, the Néel temperature of main phase and the Curie temperature of impurity phase was increased...
متن کاملرفتار ناهنجار مغناطوتنگش و پذیرفتاری مغناطیسی متناوب در بسبلورهای Gd1-xPrxCo5
Magnetostriction and low field ac-susceptibility of polycrystalline Gd1-xPrxCo5 (x = 0, 0.1 and 0.5) alloys are measured in temperature region of 77-300 K. XRD patterns show that our samples are single phase. For x = 0 (GdCo5) there are no anomaly in temperature dependence of magnetostriction and ac-susceptibility curves. For x = 0.1 and 0.5 temperature dependence of ac-susceptibilities show ea...
متن کاملMagnetostriction of Ni2Mn1−xCrxGa Heusler Alloys
Among the functionalities of magnetic Heusler alloys, magnetostriction is attracting considerable attention. The alloy Ni2MnGa has a premartensite phase, which is a precursor state to the martensitic transition. Some researchers have observed magnetostriction in this alloy in the premartensite phase. We performed magnetostriction studies on the premartensite phase of related Cr-substituted Ni2M...
متن کامل