Preparation of single-crystalline platinum nanowires with small diameters under mild conditions.
نویسندگان
چکیده
We report a convenient method to synthesize single-crystalline platinum nanowires with high aspect ratio of ca. 2.0 nm diameter by sophisticated and precise control of Pt(0) nuclei and their growth.
منابع مشابه
A laser ablation method for the synthesis of crystalline semiconductor nanowires
A method combining laser ablation cluster formation and vapor-liquid-solid (VLS) growth was developed for the synthesis of semiconductor nanowires. In this process, laser ablation was used to prepare nanometer-diameter catalyst clusters that define the size of wires produced by VLS growth. This approach was used to prepare bulk quantities of uniform single-crystal silicon and germanium nanowire...
متن کاملHighly efficient synthesis of aromatic azos catalyzed by unsupported ultra-thin Pt nanowires.
Aromatic azos were synthesized using unsupported ultra-thin platinum nanowires as catalysts under mild reaction conditions and the reaction mechanism was proposed.
متن کاملSynthesis of cobalt nanowires in aqueous solution under an external magnetic field
In contrast to the majority of related experiments, which are carried out in organic solvents at high temperatures and pressures, cobalt nanowires were synthesized by chemical reduction in aqueous solution with the assistance of polyvinylpyrrolidone (PVP) as surfactant under moderate conditions for the first time, while an external magnetic field of 40 mT was applied. Uniform linear cobalt nano...
متن کاملDiameter-controlled synthesis of single-crystal silicon nanowires
Monodisperse silicon nanowires were synthesized by exploiting well-defined gold nanoclusters as catalysts for one-dimensional growth via a vapor–liquid–solid mechanism. Transmission electron microscopy studies of the materials grown from 5, 10, 20, and 30 nm nanocluster catalysts showed that the nanowires had mean diameters of 6, 12, 20, and 31 nm, respectively, and were thus well defined by th...
متن کاملSingle-crystalline vanadium dioxide nanowires with rectangular cross sections.
We report the synthesis of single-crystalline VO2 nanowires with rectangular cross sections using a vapor transport method. These nanowires have typical diameters of 60 (+/-30) nm and lengths up to >10 mum. Electron microscopy and diffraction measurements show that the VO2 nanowires are single crystalline and exhibit a monoclinic structure. Moreover, they preferentially grow along the [100] dir...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Chemical communications
دوره 3 شماره
صفحات -
تاریخ انتشار 2007