Optical and Vibrational Spectra of CsCl-Enriched GeS2-Ga2S3 Glasses
نویسندگان
چکیده
Optical and FTIR spectroscopy was employed to study the properties of 80GeS2-20Ga2S3-CsCl chalcohalide glasses with CsCl additives in a temperature range of 77-293 K. It is shown that CsCl content results in the shift of fundamental absorption edge in the visible region. Vibrational bands in FTIR spectra of (80GeS2-20Ga2S3)100 - х (СsCl) x (x = 5, 10, and 15) are identified near 2500 cm(-1), 3700 cm(-1),, around 1580 cm(-1), and a feature at 1100 cm(-1). Low energy shifts of vibrational frequencies in glasses with a higher amount of CsCl can be caused by possible thermal expansion of the lattice and nanovoid agglomeration formed by CsCl additives in the inner structure of the Ge-Ga-S glass.
منابع مشابه
Moldable multispectral glasses in GeS2–Ga2S3–CsCl system transparent from the visible up to the thermal infrared regions
متن کامل
Second-order optical nonlinearity and ionic conductivity of nanocrystalline GeS2-Ga2S3-LiI glass-ceramics with improved thermo-mechanical properties.
IR-transparent chalcogenide glass-ceramics were fabricated through a careful ceramization process of the as-prepared 65 GeS(2) x 25 Ga(2)S(3) x 10 LiI glasses at a temperature of 403 degrees C for various durations. Owing to the precipitation of Li(x)Ga(y)S(z) crystals with a Ga(2)S(3)-like structure, clear second-harmonic generation was observed in the sample crystallized at 403 degrees C for ...
متن کاملIR Li2Ga2GeS6 nanocrystallized GeS2-Ga2S3-Li2S electroconductive chalcogenide glass with good nonlinearity
GeS(2)-Ga(2)S(3)-Li(2)S electroconductive glasses were prepared by the conventional melt-quenching method through carefully controlling the heating rate. Comparing with the reference of glass-forming region, our investigated GeS(2)-Ga(2)S(3)-Li(2)S system was extended to the cation ratio of 0-20% Li with around 40% Ga. GeS(2)-Ga(2)S(3)-Li(2)S glass-ceramics containing IR Li2Ga2GeS6 nonlinear na...
متن کاملOptical and Thermal Properties of Mixed Alkali Phosphate Based Glasses
Glassy samples with a composition of 40P2O5–30V2O5–(30-x)Li2O– xK2O, 0<x<30 (mol %) were prepared by the conventional melt quenching technique in two forms of bulk and blown film. X-ray diffraction patterns corroborated the amorphous feature of the samples. Density of samples was investigated by using Archimedes principle. Based on absorption and reflection spectra, indirect a...
متن کاملOptical characterization of BK7 borosilicate glasses containing different amounts of CeO2
Borosilicate BK7 glasses doped with different amounts of CeO2 (0.5,1,1.5%) were prepared by the convenient melting process in this work. DTA analysis proved that 0.5-1% CeO2 has a network modifier role and then up to 1.5% it shows network former role.For structural studies, FT-IR and Raman spectroscopy were carried out. Fermi energy level, direct/ indirect optical band gap and Urbach energy wer...