Effect of application time of colloidal platinum nanoparticles on the microtensile bond strength to dentin.
نویسندگان
چکیده
The purpose of this study was to investigate the effect of application time of colloidal platinum nanoparticles (CPN) on bond strength. Dentin surfaces were subjected to one of the following treatments: (A) Etching with 10% citric acid-3% FeCl(3 )solution (10-3 solution); (B) Etching with 10-3 solution followed by applying CPN as a primer solution for 10, 20, 30, or 60 seconds; and (C) Priming with CPN for 10, 20, 30, or 60 seconds followed by etching with 10-3 solution. An acrylic rod was bonded to each treated dentin surface using 4-META/MMA-TBB resin. Bonded specimens were sectioned into beams for microtensile bond strength testing. In groups (B) and (C), highest bond strength was obtained when dentin surfaces were treated with CPN for 30 seconds. This meant that the CPN primer solution either enhanced the penetration of resin into dentin or the degree of conversion of 4-META/MMA-TBB resin. Within the limitations of this study, treatment with 0.1 mN CPN primer solution followed by 20 seconds of water rinsing resulted in high bond strength.
منابع مشابه
Sodium fluoride addition to a two-step etch-and-rinse adhesive system: effect on dentin microtensile bond strength and durability
Introduction: Studies have suggested that sodium fluoride (NaF) has an inhibitory effect on the activity of endogenous matrix metalloproteinase enzymes. This study assessed the effect of a fluoride-containing adhesive on microtensile bond strength (µTBS) over time. Material & Methods: In this experimental study, 36 extracted third molars were used to evaluate the µTBS of...
متن کاملMicrotensile bond strength of clearfil SE bond to caries-affected dentin and normal dentin
Microtensile bond strength of clearfil SE bond to caries-affected dentin and normal dentin Dr. A. Ghasemi* - Dr. M. Bargrizan** - Dr. M. Mahmoodi*** *- Assistant Professor of Operative Dentistry Dept. - Faculty of Dentistry – Shaheed Beheshti University of Medical Sciences. **- Assistant Professor of Pedodontics Dept. - Faculty of Dentistry – Shaheed Beheshti University of Medical Sciences. ***...
متن کاملEffect of different synthetic matrix metalloproteinase inhibitors on composite-dentin microtensile bond strength durability
Background and Aims: Despite patient’s demand increased for tooth color restorations, the stable bond between dentin and composite is a challenge in dentistry. Dentin protease activation is responsible for dentin-resin bond failure. The aim of this study was to determine the best pretreatment agent to inhibit matrix metalloproteinase and increase resin-dentin bond durability. Materials and Met...
متن کاملبررسی اثر استفاده مجدد از میکروبراش بر استحکام باند ریزکششی ادهزیو به عاج
Background and Aims: Re-application of microbrush may affect the micro tensile bond strength of adhesives to dentin. The aim of this study was to evaluate the effect of re-application of microbrushes on the micro tensile bond strength of an adhesive to dentin.Materials and Methods: Thirty freshly extracted molars teeth were collected and enamel of occlusal surface were removed to expose superfi...
متن کاملDentin bonding agent with improved bond strength to dentin through incorporation of sepiolite nanoparticles
BACKGROUND The study aims to investigate the effect of incorporation of sepiolite nanoparticles on the microtensile bond strength of an experimental dentin bonding to the human dentin. MATERIAL AND METHODS The sepiolite nanoparticles were incorporated into an experimental methacrylate-based dentin bonding system in concentrations of 0.0, 0.2, 1.0, 2.0, and 5.0 weight percents. The specimens w...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Dental materials journal
دوره 29 6 شماره
صفحات -
تاریخ انتشار 2010