Preparation and Characterization of Organic-Inorganic Hybrid Hydrogel Electrolyte Using Alkaline Solution
نویسندگان
چکیده
Organic-inorganic hybrid hydrogel electrolytes were prepared by mixing hydrotalcite, cross-linked potassium poly(acrylate) and 6 M KOH solution. The organicinorganic hybrid hydrogel electrolytes had high ionic conductivity (0.456–0.540 S cm) at 30 °C. Moreover, the mechanical strength of the hydrogel electrolytes was high enough to form a 2–3 mm thick freestanding membrane because of the reinforcement with hydrotalcite.
منابع مشابه
Preparation and Characterization of Colloidal Silica in Alkaline and Constant Range of pH
In this study, alkaline colloidal silica was prepared by titration of an alkaline solution such as sodium silicate with silicic acid in constant range of pH .This constant range of pH was achieved by using concentrated soduim silicate solutions as pH adjusting solutions during titration.The sodium silicate solutions having a variety of...
متن کاملPreparation and Characterization of a Cotton-Based Nanocomposite Hydrogel
In this work, hydrogel nanocomposites were synthesized by solution polymerization of acrylic acid (AA) and itaconic acid (IA) in the presence of cotton fabric. Ammonium persulfate (APS) was used as the polymerization initiator in the presence of a crosslinker, methylene bisacrylamide (MBA). Insertion of Ag followed by reduction of Ag+ cations results in a hydrogel nanocomposite. The ...
متن کاملConductive Polythiophene Nanoparticles Deposition on Transparent PET Substrates: Effect of Modification with Hybrid Organic-inorganic Coating (RESEARCH NOTE)
In this work, Poly(ethyleneterephthalate) (PET) substrate was treated using KOH solution and was modified using hybrid O-I coating containing PCL )polycaprolactone( as organic phase and TEOS )tetraethoxysilane( as inorganic phase. The coating was prepared through a sol-gel process and applied on the surface by dip coater. Then, electrically conducting polythiophene (PTh) nanoparticles were depo...
متن کاملPreparation and Characterization of ZrO2/ZnO Nanocomposite under Ultrasonic Irradiation via Sol-gel Route
Nanocomposite of ZrO2/ZnO was prepared under ultrasonic irradiation by sol gel process from directly mixing Zirconium and Zinc gels, and the mixture was placed under ultrasonic irradiation for 2 hours then aging time the filtrated composite gel was calcinated at 500°C for 3h in furnace. The precursor sol of zirconium was prepared from an aqueous solution of ZrCl4 and zinc acetate dihydrated was...
متن کاملPreparation and Characterization of ZrO2/ZnO Nanocomposite under Ultrasonic Irradiation via Sol-gel Route
Nanocomposite of ZrO2/ZnO was prepared under ultrasonic irradiation by sol gel process from directly mixing Zirconium and Zinc gels, and the mixture was placed under ultrasonic irradiation for 2 hours then aging time the filtrated composite gel was calcinated at 500°C for 3h in furnace. The precursor sol of zirconium was prepared from an aqueous solution of ZrCl4 and zinc acetate dihydrated was...
متن کامل