Photoinduced Magnetization in a Thin Fe-CN-Co Film
نویسندگان
چکیده
The magnetization of a thin Fe-Co cyanide film has been investigated from 5 K to 300 K and in fields up to 500 G. Upon illumination with visible light, the magnetization of the film rapidly increases. The original cluster glass behavior is further developed in the photoinduced state and shows substantial changes in critical temperature and freezing temperature. © 2001 Elsevier Science. All rights reserved
منابع مشابه
Effect of Cobalt Concentration on Structural and Magnetic Properties of Co-Fe Thin Films
Co-Fe films were electrodeposited on Cu substrate from electrolytes with different Co concentration levels. X-ray diffraction (XRD) was used to investigate the films crystal structures. The results indicate that if the Co concentration is less that the Fe concentration, the cubic structure appears in the films, while the hexagonal structure dominates when the C...
متن کاملSynthesis, Characterization and Investigation of Magnetic Properties of Co3O4/CoFe2O4 Nanocomposite Prepared by Calcination of [CO(SALEN)(PPH3)(H2O)]4[Fe(CN)6] and [Co(Salophen)(PPH3)(H2O)]4[Fe(CN)6] Binary Complex Salts
In this research the synthesis of [Co(Salen)(PPh3)(H2O)]4[Fe(CN)6] and [Co(Salophen)(PPh3)(H2O)]4[Fe(CN)6] schiff base complexes was reported. Co3O4/CoFe2O4 magnetic nanoparticles were prepared by calcination of these complexes at 500, 550 and 600°C. Precursor complexes were identified by FT-IR and UV-Vis spectroscopy and their thermal behavior was studied via TG/DTA. Nanomagnetic samples were ...
متن کاملSoft Magnetic Properties of High-Entropy Fe-Co-Ni-Cr-Al-Si Thin Films
Soft magnetic properties of Fe-Co-Ni-Al-Cr-Si thin films were studied. As-deposited Fe-Co-Ni-Al-Cr-Si nano-grained thin films showing no magnetic anisotropy were subjected to field-annealing at different temperatures to induce magnetic anisotropy. Optimized magnetic and electrical properties of Fe-Co-Ni-Al-Cr-Si films annealed at 200 ◦C are saturation magnetization 9.13 × 105 A/m, coercivity 79...
متن کاملEvolution of magnetization reversal mechanism in Fe-Cr alloy films
A large thin film sample of FexCr1−x alloy with a composition gradient x=0.38−0.52 has been prepared by co-sputtering to investigate magnetic anisotropy and magnetization effects on reversal mechanisms. The single-phased Fe-Cr films have a bcc structure with 110 preferred orientation. Since the magnetization decreases as the Fe content is decreased and the uniaxial anisotropy energy keeps at al...
متن کاملPreparation and characterization of nanostructured S and Fe co-doped TiO2 thin film by ultrasonic-assisted spray pyrolysis method
Nanostructured TiO2 and S and Fe co-doped TiO2 thin films with high transparency were prepared on glass substrate through ultrasonic-assisted spray pyrolysis technique. The effects of doping on morphological, optical an...
متن کامل