Termite Resistance of MDF Panels Treated with Various Boron Compounds
نویسندگان
چکیده
In this study, the effects of various boron compounds on the termite resistance of MDF panels were evaluated. Either borax (BX), boric acid (BA), zinc borate (ZB), or sodium perborate tetrahydrate (SPT) were added to urea-formaldehyde (UF) resin at target contents of 1%, 1.5%, 2% and 2.5% based on dry fiber weight. The panels were then manufactured using 12% urea-formaldehyde resin and 1% NH(4)Cl. MDF samples from the panels were tested against the subterranean termites, Coptotermes formosanus Shiraki. Laboratory termite resistance tests showed that all samples containing boron compounds had greater resistance against termite attack compared to untreated MDF samples. At the second and third weeks of exposure, nearly 100% termite mortalities were recorded in all boron compound treated samples. The highest termite mortalities were determined in the samples with either BA or BX. Also, it was found that SPT showed notable performance on the termite mortality. As chemical loadings increased, termite mortalities increased, and at the same time the weight losses of the samples decreased.
منابع مشابه
The Effects of Boron Compounds and Different Melamine Contents in Muf Resins on Some Properties of Mdf Panels
The objective of this study was to determine the effects of some boron compounds, which have fire retardant properties, as well as melamineurea-formaldehyde (MUF) resins having different melamine contents (10%, 15%, and 20%) on some physical and mechanical properties of medium density fiberboard (MDF) panels. It was found that the water absorption (WA) and thickness swelling (TS) of MDF panels ...
متن کاملPhysical and mechanical properties and fire, decay, and termite resistance of treated oriented strandboard
This study evaluated the effects of a number of chemicals on the physical and mechanical properties and fire, decay, andtermite resistance of oriented strandboard (OSB) panels. Disodium octaborate tetrahydrate (DOT), boric acid (BA), melamine phosphate (MP), and a BA/DOT mixture were sprayed onto the furnish at varying concentrations. Thepanels were tested for thickness swell, water absorption,...
متن کاملBiological Decay and Termite Resistance of Post- Treated Wood-Based Composites under Protected Above-Ground Conditions: A Preliminary Study after 36 Months of Exposure
Five kinds of commercially available wood-based composites (softwood plywood, hardwood plywood, medium density fiberboard, oriented strand board, and particle board, hereinafter abbreviated as SWP, HWP, MDF, OSB, and PB, respectively) post-treated with alkaline copper quat (ACQ) and copper azole (CA) were exposed to decay and subterranean termite activity under protected above-ground conditions...
متن کاملProperties of Honeycomb Paperboards Faced with Heat-Treated Thin Medium-Density Fiberboards
In this study, 4-mm-thick medium-density fiberboard (MDF) panels were heat-treated at 140 °C for 30 or 60 min and at 180 °C for 30 or 60 min. Then, 10-mm-thick lightweight honeycomb paperboards made from kraft paper (130 g/m, cell diameter of honeycomb, 14 mm; compression strength, 0.21 N/mm) were faced with the untreated and heat-treated MDF panels (thickness: 4 mm) using a two-component polyu...
متن کاملImprovement of the Durability of Heat-treated Wood against Termites
Thermal modification is an attractive alternative to improve the decay durability and dimensional stability of wood. However, thermally modified wood is generally not resistant to termite attacks, limiting the field of application of such materials. One way to overcome this drawback is to combine thermal modification treatment with an additional treatment. One such treatment is the impregnation...