The Galvanic Interaction Between a CoCrMo Alloy, Pure Titanium and Two Different Dental Amalgams with Special Attention on the Area Size
نویسندگان
چکیده
The purpose of this study was to determine the galvanic interaction between pure titanium, a CoCrMo alloy, as well as their galvanic interaction with a high copper and a conventional amalgam at different area ratios. Pure titanium, a CoCrMo alloy and two dental amalgams with different copper compositions were tested in this study in 0.9% NaCl environment of pH 7. Polarization curves were recorded for different couples with different area ratios. The conventional amalgam is more prone to galvanic corrosion than the higher copper containing amalgam in contact with the CoCrMo alloy as well as titanium. Since there is higher galvanic interaction of amalgams with CoCrMo casting alloys, either all amalgams should be exchanged with non-metallic restorations, or titanium should be chosen as casting metal for partial denture framework, if too many amalgam restorations exist in the oral cavity.
منابع مشابه
Ions released from dental amalgams in contact with titanium.
The ions released from conventional and high-copper amalgams in contact with titanium were quantitatively analyzed in a 0.9% NaCl solution at 37 degrees C when the surface area ratio of titanium/amalgam was set up as 1/10, 1/1, or 10/1. The corrosion potentials of the amalgams and titanium were measured under the same conditions. Surface analyses on the amalgams were also employed using SEM wit...
متن کاملFriction stir welding of dissimilar joint of aluminum alloy 5083 and commercially pure titanium
In this study, commercially pure titanium and aluminum alloy 5083 in connection rotational speed of 1120 rpm and a feed rate of 50 mm per minute for butt welding by friction stir welding has been successfully completed. Micro-structure, hardness and tensile test was conducted on the connection. Welding area is a composite of aluminum and titanium particles that the particles plays an important ...
متن کاملFriction stir welding of dissimilar joint of aluminum alloy 5083 and commercially pure titanium
In this study, commercially pure titanium and aluminum alloy 5083 in connection rotational speed of 1120 rpm and a feed rate of 50 mm per minute for butt welding by friction stir welding has been successfully completed. Micro-structure, hardness and tensile test was conducted on the connection. Welding area is a composite of aluminum and titanium particles that the particles plays an important ...
متن کاملEvaluation of effect of galvanic corrosion between nickel-chromium metal and titanium on ion release and cell toxicity
PURPOSE The purpose of this study was to evaluate cell toxicity due to ion release caused by galvanic corrosion as a result of contact between base metal and titanium. MATERIALS AND METHODS It was hypothesized that Nickel (Ni)-Chromium (Cr) alloys with different compositions possess different corrosion resistances when contacted with titanium abutment, and therefore in this study, specimens (...
متن کاملElectrochemical Behaviour and Galvanic Effects of Titanium Implants Coupled to Metallic Suprastructures in Artificial Saliva
The aim of the present study is to analyze the electrochemical behavior of five different dental alloys: two cobalt-chromium alloys (CoCr and CoCr-c), one nickel-chromium-titanium alloy (NiCrTi), one gold-palladium alloy (Au), and one titanium alloy (Ti6Al4V), and the galvanic effect when they are coupled to titanium implants (TiG2). It was carried out by electrochemical techniques (open circui...
متن کامل