Capacitance Reconstruction from Measured C–V in High Leakage, Nitride/Oxide MOS
نویسندگان
چکیده
A reconstruction technique of the gate capacitance from anomalous capacitance-voltage (C–V) curves in high leakage dielectric MOSFETs is presented. An RC network is used to accommodate the distributed nature of MOSFETs and an optimization technique is applied to extract the intrinsic gate capacitance. Applicability of the method is demonstrated for ultra-thin nitride/oxide (N/O 1.4 nm/0.7 nm) composite dielectric MOSFETs.
منابع مشابه
Ultra-Thin, High Quality HfO2 on Strained-Ge MOS Capacitors with Low Leakage Current
Ultra-thin HfO2 MOS capacitors on strained-Ge (s-Ge) have been fabricated with an extracted effective oxide thickness (EOT) of 4.9 Å and leakage current less than 0.2 A/cm at |VG| < 0.5 V. The CV measurements show little hysteresis and areal capacitance scaling for 50×50 to 200×200 μm devices. A high series resistance is observed, likely due to a 500 meV valence band offset between the s-Ge and...
متن کاملCharacterization of atomic layer deposition HfO2, Al2O3, and plasma- enhanced chemical vapor deposition Si3N4 as metal–insulator–metal capacitor dielectric for GaAs HBT technology
Characterization was performed on the application of atomic layer deposition (ALD) of hafnium dioxide (HfO2) and aluminum oxide (Al2O3), and plasma-enhanced chemical vapor deposition (PECVD) of silicon nitride (Si3N4) as metal–insulator–metal (MIM) capacitor dielectric for GaAs heterojunction bipolar transistor (HBT) technology. The results show that the MIM capacitor with 62 nm of ALD HfO2 res...
متن کاملGe MOS Capacitors with Thermally Evaporated HfO2 as Gate Dielectric
We have investigated the characteristics of thermally evaporated hafnium oxide HfO2 films on germanium substrates. Surface roughness of the HfO2 film was studied by scanning electron microscopy. The presence of crystalline GeO2 was evident from X-ray diffraction results on as-deposited films. Capacitance–voltage C-V and current–voltage I-V measurements of the asdeposited metal-oxide semiconduct...
متن کاملCapacitance-voltage Characterization of Atomic-Layer-Deposited Al2O3/InGaAs and Al2O3/GaAs Metal –Oxide-Semiconductor Structures
ALD Al2O3/GaAs and Al2O3/In0.2Ga0.8As MOS and source-drain implanted MOSFET structure were fabricated and characterized by capacitance-voltage (CV) and current-voltage (I-V) measurements. It is shown that, after high-temperature anneal, the MOS leakage current density of the thinner (16nm) film is much higher than that of the thicker (30nm) film. The highquality Al2O3 (30nm)/In0.2Ga0.8As interf...
متن کاملDevice Performance of AlGaN/GaN MOS-HEMTs Using La2O3 high-k Oxide Gate Insulator
AlGaN/GaN metal-oxide-semiconductor high electron mobility transistors (MOS-HEMTs) using La2O3 as gate oxide by electron-beam evaporated have been investigated and compared with the regular HEMTs [1]. The La2O3 thin film achieved a good thermal stability after 200°C, 400°C and 600°C post-deposition annealing due to its high binding energy (835.7 eV) characteristics. Our measurements have shown ...