High Plastic Strain of Silica Microparticles under Electron Beam Irradiation
نویسندگان
چکیده
The studies of irradiation damage in silica are of significant interest because of its application in nuclear reactors, nuclear waste containers, optical fibers, and semiconductor devices [1,2]. Although there are a number of publication showing the effect of electrons, ions, protons, alpha-particles irradiation on microstructural changes of silica, understanding deformation behavior under applied stress of irradiated sample is still lacking [2,3]. In this work, we investigate plastic flow and failure behavior of amorphous silica particles under compressive stress inside a scanning electron microscopy (SEM).
منابع مشابه
Electron beam irradiation method to change polypropylene application: Rheology and thermomechanical properties
Irradiation of polymers is one of the most effective and economical methods for modifying their properties and for changing their applications. In this study, an extrusion grade polypropylene (PP) was treated by electron beam irradiation to produce a PP suitable for injection molding. Irradiation was carried out at different doses (0-80 kGy) under atmosphere air and at ambient temperature. Melt...
متن کاملRuminal Degradation Kinetics of Wheat Straw Irradiated by High Doses of Electron Beam
This study was conducted to evaluate the effect of electron beam irradiation at doses of 250 and 500 kGy on the chemical composition and ruminal dry matter (DM) and neutral detergent fiber (NDF) degradability of wheat straw. Nylon bags of untreated or irradiated wheat straw were suspended in the rumen of three rams for up to 72 h, and resulting data were fitted to non-linear degradation model t...
متن کاملThe effect of high-energy electron beam on drawn and undrawn high density polyethylene fibers
HDPE monofilaments were obtained using different extruders and drawn by post-extruder equipments. After solidification, drawn and undrawn monofilaments (draw ratio 7:1) were irradiated with 10 MeV electron beams in air at room temperature at 25, 50, 75, 100 and 125 kGy dose ranges to induce a network structure. HDPE crosslinking was studied on the basis of gel content measurements. The fibers w...
متن کاملTreatment of Synthetic Textile Wastewater by Combination of Coagulation/Flocculation Process and Electron Beam Irradiation
Introduction: Textile wastewaters from dyeing and finishing processes are heavily polluted with dyes, textile auxiliaries and chemicals and have a broad range of pH, high COD concentration and suspended particles. In this study, the efficiency of color and turbidity removal from synthetic textile wastewater samples were investigated by combined process of coagulation/ flocculation and electron ...
متن کاملElectron-beam-assisted superplastic shaping of nanoscale amorphous silica
Glasses are usually shaped through the viscous flow of a liquid before its solidification, as practiced in glass blowing. At or near room temperature (RT), oxide glasses are known to be brittle and fracture upon any mechanical deformation for shape change. Here, we show that with moderate exposure to a low-intensity (<1.8×10(-2) A cm(-2)) electron beam (e-beam), dramatic shape changes can be ac...
متن کامل