Magnetic properties and structure of Fe/Pt thin films
نویسندگان
چکیده
The structural transfqmation from fcc to fct and relevant magnetic properties of initially multilayered Fe/Pt films were studied. When the asdeposited FePt films were annealed at the temperature of 300°C and up, the fct-phase was formed. Rather square hysteresis loops and large coercivities were measured from the annealed films. The films annealed at 300°C retain a layered structure.
منابع مشابه
Effect of Cobalt Concentration on Structural and Magnetic Properties of Co-Fe Thin Films
Co-Fe films were electrodeposited on Cu substrate from electrolytes with different Co concentration levels. X-ray diffraction (XRD) was used to investigate the films crystal structures. The results indicate that if the Co concentration is less that the Fe concentration, the cubic structure appears in the films, while the hexagonal structure dominates when the C...
متن کاملEffect of Magnetic Field on Surface Morphology and Magnetic Properties of FeCu/Cu Nano layers Prepared by Electrodeposition Technique: Investigation of Magneto-hydrodynamic Effect
In this paper, the effect of magnetic field on the morphology, structure and magnetic properties of electrodeposited FeCu/Cu thin films was investigated. The films were deposited on Au2PdAg/glass substrates using electrodeposition technique in potentiostatic control. The magnetic fields of 5000 and 7000 Oe were applied on deposition bath during deposition. Two series of thin films were prepared...
متن کاملInfluence of Co and Fe substitution on optical and structural properties of zinc oxide thin films
Zn0.97TM0.03O (TM = Co, Fe) thin films were deposited onto glass substrates by the sol–gel method and the effects of transition metals substitution on structural and optical properties of ZnO films were investigated. The X-ray diffraction patterns revealed that the films have wurtzite structure. Optical transmittance of the films was recorded in the range of 200 -800 nm wave length and the band...
متن کاملStructural, Electrical, Magnetic and Resistive Switching Properties of the Multiferroic/Ferroelectric Bilayer Thin Films
Bi0.8Pr0.2Fe0.95Mn0.05O₃/Bi3.96Gd0.04Ti2.95W0.05O12 (BPFMO/BGTWO) bilayer thin films with Multiferroic/Ferroelectric (MF/FE) structures were deposited onto Pt(111)/Ti/SiO₂/Si(100) substrates by using the sol-gel method with rapid thermal annealing. The BPFMO/BGTWO thin films exhibited well-saturated ferromagnetic and ferroelectric hysteresis loops because of the electro-magnetic coupling induce...
متن کاملCHARACTERIZATION OF CO-FE MAGNETIC FILMS FABRICATED BY GALVANO-STATIC ELECTRODEPOSITION
In this research, nanocrystalline Co-Fe coatings were electrodeposited on copper substrate. The influence of current density on different properties of the films at two pH levels was investigated. All the coatings showed nodular structure with rougher morphology at higher current densities. Due to anomalous deposition at higher current density, the amount of iron content increased and reached i...