Bifunctional hairy silica nanoparticles as high-performance additives for lubricant
نویسندگان
چکیده
Bifunctional hairy silica nanoparticles (BHSNs), which are silica nanoparticles covered with alkyl and amino organic chains, were prepared as high-performance additives for lubricants. Compared with hairy silica nanoparticles covered by a single type of organic chain, binary hairy silica nanoparticles exhibit the advantages of both types of organic chains, which exhibit excellent compatibility with lubricants and adsorbability to metal surfaces. Nanoparticles with different ratios of amino and alkyl ligands were investigated. In comparison to an untreated lubricant, BHSNs reduce the friction coefficient and wear scar diameter by 40% and 60%, respectively. The wear mechanism of BHSNs was investigated, and the protective and filling effect of the nanoparticles improved because of collaboration of amino and alkyl ligands.
منابع مشابه
Graphite and Hybrid Nanomaterials as Lubricant Additives
Lubricant additives, based on inorganic nanoparticles coated with organic outer layer, can reduce wear and increase load-carrying capacity of base oil remarkably, indicating the great potential of hybrid nanoparticles as anti-wear and extreme-pressure additives with excellent levels of performance. The organic part in the hybrid materials improves their flexibility and stability, while the inor...
متن کاملEngineered silica nanoparticles as additives in lubricant oils
Silica nanoparticles (SiO2 NPs) synthesized by the sol-gel approach were engineered for size and surface properties by grafting hydrophobic chains to prevent their aggregation and facilitate their contact with the phase boundary, thus improving their dispersibility in lubricant base oils. The surface modification was performed by covalent binding of long chain alkyl functionalities using lauric...
متن کاملEffect of Molybdenum Disulfide Particle Sizes on Wear Performance of Commercial Lubricant
Experimental investigations have been conducted for determination of effectiveness of employing a combination of three particle sizes (40 nm size, 1.75 μm size and 53 μm size) of Molybdenum Disulphide as anti-wear additive in a commercial lubricant. The conformal block and disk configuration has been used to conduct experiments for determination of wear of the sliding surfaces. The performance ...
متن کاملSynthesis of Silica-coated Iron Oxide Nanoparticles: Preventing Aggregation Without Using Additives or Seed Pretreatment
The Stober process is frequently used to prepare silica-coated iron oxide nanoparticles. This is usually achieved by seeding a reaction mixture consisting of water, ethanol and a catalyst with iron oxide particles and adding a silica precursor. The hydrolysis and condensation of precursor monomers results in the deposition of a silica layer on iron oxide particles. However, this process is acco...
متن کاملThe investigation of different particle size magnesium-doped zinc oxide (Zn0.92Mg0.08O) nanoparticles on the lubrication behavior of paraffin oil
Magnesium-doped zinc oxide (Zn0.92Mg0.08O) (ZMO) nanoparticles of 23 nm particle size have been synthesized by auto-combustion method. The variation in particle size of these nanoparticles has been performed by their further calcination at 800 and 1000 C for 2 h and the corresponding calcined particles are designated as ZMO-1 and ZMO-2, respectively. The nanoparticles have been characterized by...