Synthesis and Characterization of Cobalt-Doped WS2 Nanorods for Lithium Battery Applications
نویسندگان
چکیده
Cobalt-doped tungsten disulfide nanorods were synthesized by an approach involving exfoliation, intercalation, and the hydrothermal process, using commercial WS2 powder as the precursor and n-butyllithium as the exfoliating reagent. XRD results indicate that the crystal phase of the sample is 2H-WS2. TEM images show that the sample consists of bamboo-like nanorods with a diameter of around 20 nm and a length of about 200 nm. The Co-doped WS2 nanorods exhibit the reversible capacity of 568 mAh g-1 in a voltage range of 0.01-3.0 V versus Li/Li+. As an electrode material for the lithium battery, the Co-doped WS2 nanorods show enhanced charge capacity and cycling stability compared with the raw WS2 powder.
منابع مشابه
NANO EXPRESS Synthesis and Characterization of Cobalt-Doped WS2 Nanorods for Lithium Battery Applications
Cobalt-doped tungsten disulfide nanorods were synthesized by an approach involving exfoliation, intercalation, and the hydrothermal process, using commercial WS2 powder as the precursor and n-butyllithium as the exfoliating reagent. XRD results indicate that the crystal phase of the sample is 2H-WS2. TEM images show that the sample consists of bamboo-like nanorods with a diameter of around 20 n...
متن کاملSynthesis and characterization of Ag doped Cobalt Ferrite nanocomposite
Nanomaterials are attracted a great deal of attention from scientific community due to its unique properties and applications. The small size ferrites have opened the door for intensive research to utilize their properties for biomedical applications. Cobalt ferrite nanomaterials and its silver doped (Ag-doped) nanocomposites have been prepared using solid state combustion method. This combusti...
متن کاملFabrication of single-layer MS2 (M=Mo, W) nanosheets using Li battery setup
Lithium intercalation is a convenient method to prepare few-layer and single-layer MS2 (M=Mo, W) nanosheets. This method is, however, very time-consuming (few days) and it is difficult to control the reaction parameters. To overcome these drawbacks, we have proposed a method to use an Li battery set-up to significantly reduce the reaction time (few hours) and electrochemically intercalate lithi...
متن کاملFabrication and Characterization of Nanoporous Co Oxide (Co3O4) Prepared by Simple Sol-gel Synthesis
Cobalt oxide (Co3O4) nanorods were prepared by a simple co-precipitation method using ethanol solution of cobalt nitrate as precursor and cetyl trimethylammonium bromide (CTAB) as surfactant. Morphological properties of the nanoparticles were characterized. XRD measurement exhibited the structure of Co3O4 nanocrystals for annealed samples. The SEM ima...
متن کاملElectrochemical Characterization of Low-Cost Lithium-Iron Orthosilicate Samples as Cathode Materials of Lithium-Ion Battery
Lithium-iron-orthosilicate is one of the most promising cathode materials for Li-ion batteries due to its safety, environmental brightness and potentially low cost. In order to produce a low cost cathode material, Li2FeSiO4/C samples are synthesized via sol-gel (SG; one sample) and solid state (SS; two samples with different carbon content), starting from Fe (III) in the raw materials (lo...