Effect of ascorbic acid, ethanol and acetone on adhesion between the treated fiber posts and composite resin cores
نویسندگان
چکیده
PURPOSE The aim of the present study was to assess the effect of ascorbic acid, ethanol and acetone on microtensile bond strength between fiber posts pre-treated with hydrogen peroxide and composite resin cores. MATERIALS AND METHODS Twenty four fiber posts were pre-treated with 24% hydrogen peroxide and divided into 4 groups as follows: G1: no treatment, as control group; G2: treatment with 10% ascorbic acid solution for 5 minutes; G3: treatment with 70% ethanol solution for 5 minutes; and G4: treatment with 70% acetone solution for 5 minutes. Each fiber post was surrounded by a cylinder-shaped polyglass matrix which was subsequently filled with composite resin. Two sections from each sample were selected for microtensile test at a crosshead with speed of 0.5 mm/min. Statistical analyses were performed using one-way ANOVA and a post hoc Tukey HSD test. Fractured surfaces were observed under a stereomicroscope at ×20 magnification. The fractured surfaces of the specimens were observed and evaluated under a SEM. RESULTS MEANS OF MICROTENSILE BOND STRENGTH VALUES (MPA) AND STANDARD DEVIATIONS IN THE GROUPS WERE AS FOLLOWS: G1: 9.70±0.81; G2: 12.62±1.80; G3: 16.60±1.93; and G4: 21.24±1.95. G4 and G1 had the highest and the lowest bond strength values, respectively. A greater bond strength value was seen in G3 compared to G2. There were significant differences between all the groups (P<.001). All the failures were of the adhesive mode. CONCLUSION Application of antioxidant agents may increase microtensile bond strength between fiber posts treated with hydrogen peroxide and composite cores. Acetone increased bond strength more than ascorbic acid and ethanol.
منابع مشابه
Erratum - Effect of ascorbic acid, ethanol and acetone on adhesion between the treated fiber posts and composite resin cores
متن کامل
In Vitro Effect of Zirconia and Zirconia Enriched Glass Fiber Composite Posts on Fracture Resistance of Endodontically Treated Teeth
Objective: Despite the advantages of esthetic posts, lack of studies on their fracture resistance has limited their clinical use. This study aimed to compare the effect of two types of esthetic posts namely zirconia and zirconia enriched glass fiber composite posts on fracture resistance of endodontically treated teeth against compressive forces. Methods: This in vitro study was conducted o...
متن کاملمقایسه اثر دو نوع پست گلاس‌فایبر و پست FRC با پوشش زیرکونیا بر مقاومت به شکست در دندان‌های اندو شده
Background and Aims : The root fracture resistance of endodontically treated teeth depends on the types of posts. The aim of this study was to compare the effect of two types of bonded non-metallic posts with different elasticity modulus on the fracture resistance of endodontically treated teeth under compressive loads. Materials and Methods: In this in vitro experimental study, 20 fresh ex...
متن کاملIn-Vitro evaluation of fracture resistance of weakened roots restored with fiber posts and tooth-colored materials
In-Vitro evaluation of fracture resistance of weakened roots restored with fiber posts and tooth-colored materials Dr. H. Moosavi* - Dr. F. Maleknejad**- Dr. I. Nasiraee*** * Assistant Professor of Operative Dentistry Dept., Faculty of Dentistry, Mashhad University of Medical Sciences. ** Associate Professor of Operative Dentistry Dept., Faculty of Dentistry, Mashhad University of Medical Scien...
متن کاملEffect of ferrule on fracture resistance in endodontically treated teeth that were restored with bonded posts and cores
Effect of ferrule on fracture resistance in endodontically treated teeth that were restored with bonded posts and cores Dr. MH. Salari * - Dr. E. Jalalian * - Dr. S. Soleimani ** * Assistant Professor of Fixed Prosthodontics Dept., Faculty of Dentistry, Azad University (Tehran). ** Dentist. Abstract Background and Aim: A dowel in an endodontically treated tooth could transfer occlusal forces in...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره 4 شماره
صفحات -
تاریخ انتشار 2012