Color-tunable up-conversion emission in Y2O3:Yb3+, Er3+ nanoparticles prepared by polymer complex solution method
نویسندگان
چکیده
Powders of Y2O3 co-doped with Yb3+ and Er3+ composed of well-crystallized nanoparticles (30 to 50 nm in diameter) with no adsorbed ligand species on their surface are prepared by polymer complex solution method. These powders exhibit up-conversion emission upon 978-nm excitation with a color that can be tuned from green to red by changing the Yb3+/Er3+ concentration ratio. The mechanism underlying up-conversion color changes is presented along with material structural and optical properties. PACS: 42.70.-a, 78.55.Hx, 78.60.-b.
منابع مشابه
Distance Dependence of Gold-Enhanced Upconversion luminescence in Au/SiO2/Y2O3:Yb3+, Er3+ Nanoparticles
We report a localized surface plasmon enhanced upconversion luminescence in Au/SiO2/Y2O3:Yb3+,Er3+ nanoparticles when excited at 980 nm. By adjusting the silica spacer's thickness, a maximum 9.59-fold enhancement of the green emission was obtained. Effect of the spacer distance on the Au-Y2O3:Yb3+, Er3+ green upconversion mechanism was numerically simulated and experimentally demonstrated. In t...
متن کاملEnhanced Photovoltaic Performance of Dye-Sensitized Solar Cells by Efficient Near-Infrared Sunlight Harvesting using Upconverting Y2O3:Er3+/Yb3+ Phosphor Nanoparticles
We report the efficiency enhancement in dye-sensitized solar cells (DSSCs) using Er(3+)/Yb(3+)-co-doped Y2O3 (i.e., Y2O3:Er(3+)/Yb(3+)) phosphor nanoparticles, prepared by a simple and cost-effective urea-based homogeneous precipitation method, for efficient near-infrared (NIR) sunlight harvesting. Under the light excitation at a wavelength of 980 nm, the as-prepared samples exhibited strong up...
متن کاملLu3+/Yb3+ and Lu3+/Er3+ Co-doped Antimony Selenide Nanomaterials: Synthesis, Characterization, Electrical, Thermoelectrical and Optical Properties
Lu3+/Yb3+ and Lu3+/Er3+ Co-doped Sb2Se3 nanomaterials were synthesized by a Co-reduction method in hydrothermal condition. Powder XRD patterns indicate that the LnxLn′xSb2-2xSe3 Ln: Lu3+/Yb3+ and Lu3+/Er3+ crystals (x= 0.00-0.04) are isostructural with Sb2Se3. The cell parameters were increased for compounds upon increasing the dopant content (x). SEM and TEM images show that Co-doping of Lu3+/...
متن کاملFacile Synthesis and Potential Bioimaging Applications of Hybrid Upconverting and Plasmonic NaGdF4: Yb3+, Er3+/Silica/Gold Nanoparticles
We present a simple method for preparing water dispersible NaGdF4: Yb3+, Er3+/silica/gold nanoparticles. The emission intensity and color of the upconverting cores are modulated by the plasmonic absorbance and field enhancement from the gold nanoparticles. The applicability of hybrid NPs for multi-modal bioimaging probes is illustrated by in vitro confocal microscopy of living cancer cells.
متن کاملLu3+/Yb3+ and Lu3+/Er3+ Co-doped Antimony Selenide Nanomaterials: Synthesis, Characterization, Electrical, Thermoelectrical and Optical Properties
Lu3+/Yb3+ and Lu3+/Er3+ Co-doped Sb2Se3 nanomaterials were synthesized by a Co-reduction method in hydrothermal condition. Powder XRD patterns indicate that the LnxLn′xSb2-2xSe3 Ln: Lu3+/Yb3+ and Lu3+/Er3+ crystals (x= 0.00-0.04) are isostructural with Sb2Se3. The cell parameters were increased for compounds upon increasing the dopant content (x). SEM and TEM images show that Co-doping of Lu3+/...
متن کامل