The Precipitation of Carbides during Tempering of High Carbon Martensite*
نویسنده
چکیده
perature range between 260° and 360°C. Jack showed that thin platelets of cementite formed at the beginning of this stage(10). In high carbon steels, the transformation twin interfaces are potent nucleation sites for the cementite formation and the cementite is related to the ferrite by Bagaryatskii's orientation relationship(2)(3)(11). Although there is no direct evidence of its existence in steels, Nagakura et al.(5)(6), Duggin et al.(12)(13), and
منابع مشابه
Grain Refinement of Dual Phase Steel via Tempering of Cold-Rolled Martensite
A microstructure consisting of ultrafine grained (UFG) ferrite with average grain size of ~ 0.7 µm and dispersed nano-sized carbides was produced by cold-rolling and tempering of the martensite starting microstructure in a low carbon steel. Subsequently, fine grained dual phase (DP) steel consisting of equiaxed ferrite grains with average size of ~ 5 µm and martensite islands with average size ...
متن کاملInfluence of Tempering on the Microstructure & Properties of Martensite and Bainite developed in a Low-C High-Si Steel
Martensitic and bainitic steels are two types of widely used steels with excellent mechanical behaviors in automatic industry. It’s universally acknowledged that asquenched martensite possesses poor ductility and impact toughness, which should be tempered before putting into application. During tempering, as-quenched martensite changes from a hard and brittle microstructure to more ductile and ...
متن کاملExamination of carbon partitioning into austenite during tempering of bainite
The redistribution of carbon after tempering of a novel nanocrystalline bainitic steel consisting of a mixture of supersaturated ferrite and retained austenite has been analyzed by atom probe tomography. No direct evidence supporting the additional carbon enrichment of austenite beyond that initially achieved during the bainite heat treatment was obtained during subsequent tempering of this hig...
متن کاملTempering of hard mixture of bainitic ferrite and austenite
Recent work has shown that bainitic ferrite plates produced by transformation at low temperatures can be as thin as 20 nm with a hardness in excess of 650 HV30, tensile strengthy2.3 GPa and toughnessy30 MPa m. Because these properties rely on the fine scale of the microstructure, a study has been carried out in relation to the tempering resistance of steel over the temperature range 350 – 750uC...
متن کاملMicrostructure Design of Tempered Martensite by Atomistically Informed Full-Field Simulation: From Quenching to Fracture
Martensitic steels form a material class with a versatile range of properties that can be selected by varying the processing chain. In order to study and design the desired processing with the minimal experimental effort, modeling tools are required. In this work, a full processing cycle from quenching over tempering to mechanical testing is simulated with a single modeling framework that combi...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره شماره
صفحات -
تاریخ انتشار 2010