Combined effect of rapid nitriding and plastic deformation on the surface strength, toughness and wear resistance of steel 38CrMoAlA
نویسنده
چکیده
The combined treatment of pressurized gas nitriding and cold rolling is proposed as a new approach to rapid preparation of a strong and tough nitrided layer for steel 38CrMoAlA. The microstructural characteristics and properties of the modified surface layer in comparison with those of the conventionally gas nitrided sample have systematically been evaluated. The results show that the hardness and toughness of the nitrided surface layer can be significantly improved by the combined treatment. Especially, the wear resistance of nitrided surface layer under heavy loads was greatly enhanced. It can provide a new approach to rapidly preparing a nitrided layer with high strength and toughness.
منابع مشابه
The Effect to Epsilon Phase on the Friction and Wear of Nitrided Die Steels (RESEARCH NOTE)
In this paper, the wear resistance and antifriction of epsilon phase layer and diffusion layer of gas nitrided D2 steel and M2 steel have been studied. The changes m wear mechanism of epsilon phase under the load from 20N to 200N are analysed. When the load is lighter than 100N, it is mainly oxidizing wear on friction surface. The adhesion, peeling off and abrasive wear appear on friction surfa...
متن کاملINFLUENCE OF SURFACE NANO/ULTRAFINE STRUCTURE ACHIEVED BY DEEP ROLLING PROCESS ON PLASMA NITRIDING AND TRIBOLOGICAL PROPERTIES OF THE AISI 316L STAINLESS STEEL
Influence of formation of surface nano/ultrafine structure using deep rolling on plasma nitriding and tribological properties of the AISI 316L stainless steel was investigated. Initially, the deep rolling process was carried out on the bar-shaped specimens at 15 cycles with 0.2 mm/s longitudinal rate and 22.4 rpm bar rotation. Then, plasma nitriding treatment was applied on the as-received...
متن کاملDuplex Surface Treatment of AISI 1045 Steel via Plasma Nitriding of Titanized Layer
In this Study, surface of medium carbon steel (AISI 1045) was modified by titanizing followed by plasma nitriding. Titanizing was performed using pack cementation method, in a pack mixture of ferrotitanium, ammonium chloride and alumina, at 1223 K for 45 and 180 min. Plasma-nitriding was conducted at two temperatures of 803 and 823 K for 5 h, in a gas mixture of 75%N2+25%H2. The samples were c...
متن کاملEffect of SiC nanoparticles addition on mechanical properties and wear resistance of cemented carbides fabricated by spark plasma sintering
WC-10Co cemented carbides containing 1 to 4 wt% SiC nanoparticles were prepared by spark plasma sintering. The effects of SiC content on microstructure, mechanical properties and wear resistance of the sintered materials were studied. Microstructural studies showed that SiC addition resulted in WC grain coarsening. In addition, the hardness decreased with increasing SiC content. However, the fr...
متن کاملSTUDY THE WEAR MECHANISM OF A PLASMA ELECTROLYTIC NITROCARBURISED (PEN/C) 316L AUSTENITIC STAINLESS STEEL
The wear mechanism of plasma electrolytic nitrocarburised (PEN/C) 316L stainless steel samples was studied after a pin on disc wear test. The surface morphology of samples after application of PEN/C process was studied using scanning electron microscope technique. The sliding tracks resulting from the wear tests on the treated specimens indicated no signs of plastic deformation and adhesive wea...
متن کامل