Al-Doped ZnO Thin Film Transistors by Thermal Evaporation
نویسندگان
چکیده
In this paper, Al-doped ZnO thin film transistors (AZO-TFT) were fabricated by the thermal evaporation growth of AZO channel layer on a silicon substrate at temperatures below 250°C. A SiO2 dielectric layer grown by the horizontal furnace was used as a gate. An active layer thickness of 10nm was measured by Atomic Force Microscopy (AFM), and its surface had root mean square (rms) roughness 12.688 nm, and crystallize height between 81.081 nm ~ 41.285 nm.
منابع مشابه
Al Doped ZnO Thin Films; Preparation and Characterization
ZnO is a promising material suitable for variety of novel electronic applications including sensors, transistors, and solar cells. Intrinsic ZnO film has inferiority in terms of electronic properties, which has prompted researches and investigations on doped ZnO films in order to improve its electronic properties. In this work, aluminum (Al) doped ZnO (AZO) with various concentrations and undop...
متن کاملInverted Organic Solar Cells with Low-Temperature Al-Doped-ZnO Electron Transport Layer Processed from Aqueous Solution
The aqueous-based Zn-ammine complex solutions represent one of the most promising routes to obtain the ZnO electron transport layer (ETL) at a low temperature in inverted organic solar cells (OSCs). However, to dope the ZnO film processed from the Zn-ammine complex solutions is difficult since the introduction of metal ions into the Zn-ammine complex is a nontrivial process as ammonium hydroxid...
متن کاملDMMP Sensing Performance of Undoped and Al Doped Nanocrystalline ZnO Thin Films Prepared by Ultrasonic Atomization and Pyrolysis Method
Highly textured undoped (pure) and Al doped ZnO nanocrystalline thin films prepared by ultrasonic atomization and pyrolysis method are reported in this paper. ZnCl2 water solution was converted into fine mist by ultrasonic atomizer (Gapusol 9001 RBI Meylan, France). The mist was pyrolyzed on the glass substrates in horizontal quartz reactor placed in furnace. The Structural and microstructural ...
متن کاملLow-Concentration Indium Doping in Solution-Processed Zinc Oxide Films for Thin-Film Transistors
We investigated the influence of low-concentration indium (In) doping on the chemical and structural properties of solution-processed zinc oxide (ZnO) films and the electrical characteristics of bottom-gate/top-contact In-doped ZnO thin-film transistors (TFTs). The thermogravimetry and differential scanning calorimetry analysis results showed that thermal annealing at 400 °C for 40 min produces...
متن کاملHigh-performance ZnO nanowire transistors with aluminum top-gate electrodes and naturally formed hybrid self-assembled monolayer/AlO(x) gate dielectric.
A method for the formation of a low-temperature hybrid gate dielectric for high-performance, top-gate ZnO nanowire transistors is reported. The hybrid gate dielectric consists of a self-assembled monolayer (SAM) and an aluminum oxide layer. The thin aluminum oxide layer forms naturally and spontaneously when the aluminum gate electrode is deposited by thermal evaporation onto the SAM-covered Zn...