Fabrication and evaluation of Bis-GMA/TEGDMA resin with various amounts of silane-coated silica for orthodontic use.

نویسندگان

  • Owais Khalid Durrani
  • Ulfat Bashir
  • Noeen Arshad
چکیده

The objective of this research was to fabricate a composite with an optimum filler level in a bisphenol-A-glycidyldimethacrylate (Bis-GMA) triethylene glycidal dimethacrylate (TEGDMA) resin for bonding of metallic orthodontic brackets to achieve the best handling characteristics with optimum bond strength and without compromising the mechanical properties of the adhesive. One-hundred and sixty extracted human premolars free of any detectable pathology or buccal surface alterations were collected and divided into four groups. In group 1 (control), the teeth were bonded with stainless steel brackets using Transbond XT. In groups 2, 3, and 4, the teeth were bonded with metal brackets using a Bis-GMA/TEGDMA resin with 80, 60, and 20 per cent by weight silane-coated silica of a spherical shape with a mean size of 0.01 μm. Shear bond strength (SBS) of the composites was determined and the adhesive remnant index (ARI) and enamel fracture post-debonding were assessed. According to one-way analysis of variance and Tukey's honestly significant difference (HSD) multiple comparison tests, the SBS of group 4 (10.54 MPa) was considerably less than that of groups 1 (26.1 MPa), 2 (25.5 MPa), and 3 (24.6 MPa). Chi-square analysis revealed that there was an insignificant difference in the incidence of enamel fracture between groups 1 and 2, while a significant difference was present between groups 1 and 2 and 3 and 4. An insignificant difference was also observed in the location of the adhesive failure between the four groups. While all the bonding adhesives tested can be safely used for bonding of brackets, 60 per cent filled Bis-GMA/TEGDMA was superior clinically due to its ease of handling and superior bond strength.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Cellulose Nanofibre Mesh for Use in Dental Materials

The aim of this study was to produce a 3D mesh of defect free electrospun cellulose acetate nanofibres and to use this to produce a prototype composite resin containing nanofibre fillers. This might find use as an aesthetic orthodontic bracket material or composite veneer for restorative dentistry. In this laboratory based study cellulose acetate was dissolved in an acetone and dimethylacetamid...

متن کامل

The evaluation of residual monomer released after polymerization of four different composite resins

Purpose: The aim of this study is to compare the amount of Bis-GMA, UDMA, and TEGDMA released from four different types of composite resins in three different time periods using the HPLC device. Materials and Methods: Four different composite resin materials with nanofiller content were used in the study. A total of 40 sample discs were prepared and polished to provide 10 pieces for each mater...

متن کامل

Preparation of a Bis-GMA-Free Dental Resin System with Synthesized Fluorinated Dimethacrylate Monomers

With the aim of reducing human exposure to Bisphenol A (BPA) derivatives in dentistry, a fluorinated dimethacrylate monomer was synthesized to replace 2,2-bis[4-(2-hydroxy-3-methacryloy-loxypropyl)-phenyl]propane (Bis-GMA) as the base monomer of dental resin. After mixing with reactive diluent triethyleneglycol dimethacrylate (TEGDMA), fluorinated dimethacrylate (FDMA)/TEGDMA was prepared and c...

متن کامل

Adherence of Streptococcus mutans and Adsorption of Salivary Protein to Resin Composites Containing S-PRG Fillers

The purpose of this study was to measure the amount of adsorption of various salivary proteins to a resin composite having various amounts of surface pre-reacted glass-ionomer (S-PRG) fillers, and to make a comparative study of the adherence of S. mutans to the resin composite covered by various salivary proteins. We experimentally produced resin composites (S-PRG resin) having the basic compos...

متن کامل

Investigation of the mechanical properties of a low-shrinkage liquid crystalline matrix combined with nano-hydroxyapatite

The objective of this study was to investigate the mechanical properties of a low-shrinkage acrylate liquid crystalline resin matrix (ALCRM), (4-3-(acryloyloxy)-2-hydroxypropoxy) phenyl 4-(3-(acryloyloxy)-2-hydroxypropoxy) benzoate, combined with nano-hydroxyapatite (na-HA). The ALCRM monomer and diluent monomer triethylene glycol dimethacrylate (TEGDMA) were mixed at a mass ratio of 7:3 to pre...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:
  • European journal of orthodontics

دوره 34 1  شماره 

صفحات  -

تاریخ انتشار 2012