Electrocatalyst decorated hematite nanowire arrays for photoelectrochemical water splitting
نویسنده
چکیده
منابع مشابه
Silicon/hematite core/shell nanowire array decorated with gold nanoparticles for unbiased solar water oxidation.
We report the facile fabrication of three-dimensional (3D) silicon/hematite core/shell nanowire arrays decorated with gold nanoparticles (AuNPs) and their potential application for sunlight-driven solar water splitting. The hematite and AuNPs respectively play crucial catalytic and plasmonic photosensitization roles, while silicon absorbs visible light and generates high photocurrent. Under sim...
متن کاملPhotoelectrochemical activity of as-grown, α-Fe2O3 nanowire array electrodes for water splitting.
Undoped hematite nanowire arrays grown using plasma oxidation of iron foils show significant photoactivity (~0.38 mA cm(-2) at 1.5 V versus reversible hydrogen electrode in 1 M KOH). In contrast, thermally oxidized nanowire arrays grown on iron exhibit no photoactivity due to the formation of a thick (>7 μm Fe(1-x)O) interfacial layer. An atmospheric plasma oxidation process required only a few...
متن کاملSurface Engineered Doping of Hematite Nanorod Arrays for Improved Photoelectrochemical Water Splitting
Given the narrow band gap enabling excellent optical absorption, increased charge carrier density and accelerated surface oxidation reaction kinetics become the key points for improved photoelectrochemical performances for water splitting over hematite (α-Fe2O3) photoanodes. In this study, a facile and inexpensive method was demonstrated to develop core/shell structured α-Fe2O3 nanorod arrays. ...
متن کاملCarbon quantum dots decorated Cu2S nanowire arrays for enhanced photoelectrochemical performance.
The photoelectrochemical (PEC) performance of Cu2S nanowire arrays (NWAs) has been demonstrated to be greatly enhanced by dipping-assembly of carbon quantum dots (CQDs) on the surfaces of Cu2S NWAs. Experimental results show that the pristine Cu2S NWAs with higher aspect ratios exhibit better PEC performance due to the longer length scale for light absorption and the shorter length scale for mi...
متن کاملEnhancing Water Splitting Activity and Chemical Stability of Zinc Oxide Nanowire Photoanodes with Ultrathin Titania Shells
Zinc oxide nanowire photoanodes are chemically stabilized by conformal growth of an ultrathin shell of titania through atomic layer deposition, permitting their stable operation for water splitting in a strongly alkaline solution. Because of the passivation of zinc oxide surface charge traps by titania coating, core/shell nanowire arrays supply a photocurrent density of 0.5 mA/cm under simulate...