Layer-by-Layer Structured Membranes of Silk Fibroin and Polyethylen- imine on Electrospun Silk Fibroin Nanofibers
نویسندگان
چکیده
Self-assembled silk fibroin (SF)-polyethylenimine (PEI) multilayered films were fabricated on ethanol treated electrospun SF nanofibrous substrates via the electrostatic layer-by-layer (LBL) adsorption. The film coated membranes were characterized using scanning electron microscopy (SEM), transmission electron microscope (TEM) and X-ray photoelectron spectrophotometer (XPS). The SEM images showed that the multilayers of SF-PEI were formed on the surface of the ethanol treated SF nanofibres. The characteristics such as the fiber shape and porous structure were well maintained as the number of the coated SF-PEI bilayers was less than five. However, obvious adhesive substances and blocked pores were observed on the surface of the fibers as the number of bilayers of SF-PEI increased to six. Furthermore, the obvious core-shell structures were observed by TEM. The thickness of five SF-PEI bilayers was approximately 80nm. Additionally, the XPS results also revealed that the SF-PEI multilayer composite membranes formed. The adsorption mainly depended on a simple electrostatic interaction between the layers of SF and PEI. These SF-PEI multilayer assembled nanofibrous membranes could be a promising material for use as a sensor, gene delivery agent and scaffolds.
منابع مشابه
Electrospun silk fibroin nanofibers promote Schwann cell adhesion, growth and proliferation
In this study, Schwann cells, at a density of 1 × 10(5) cells/well, were cultured on regenerated silk fibroin nanofibers (305 ± 84 nm) prepared using the electrospinning method. Schwann cells cultured on the silk fibroin nanofibers appeared more ordered, their processes extended further, and they formed more extensive and complex interconnections. In addition, the silk fibroin nanofibers had no...
متن کاملAnalysis of the Comprehensive Tensile Relationship in Electrospun Silk Fibroin/Polycaprolactone Nanofiber Membranes
The mechanical properties of electrospun nanofiber membranes are critical for their applications. A clear understanding of the mechanical properties that result from the characteristics of the individual fiber and membrane microstructure is vital in the design of fiber composites. In this reported study, silk fibroin (SF)/polycaprolactone (PCL) composite nanofiber membranes were preparedusing a...
متن کاملFabrication and Biocompatibility of Electrospun Silk Biocomposites
Silk fibroin has attracted great interest in tissue engineering because of its outstanding biocompatibility, biodegradability and minimal inflammatory reaction. In this study, two kinds of biocomposites based on regenerated silk fibroin are fabricated by electrospinning and post-treatment processes, respectively. Firstly, regenerated silk fibroin/tetramethoxysilane (TMOS) hybrid nanofibers with...
متن کاملElectrospun silk-based nanofibrous scaffolds: fiber diameter and oxygen transfer.
In this study, silk fibroin was extracted from cocoons of silkworms and fabricated into nonwoven mats by electrospinning method. A new model based on the group method of data handling (GMDH) and artificial neural network (ANN) was developed for estimation of the average diameter of electrospun silk fibroin nanofibers. In this regard, concentration, flow rate, voltage, distance, and speed of col...