A performance-based evaluation of chemically similar (carbonate) tempers from Late Prehistoric (AD 1200-1700) Ohio: Implications for human selection and production of ceramic technology

PURPOSE This study was designed to assess the mechanical properties of two calcium carbonate tempers, limestone and burnt shell. These tempers have been previously compared, in separate studies, to silicate-based grit or sand temper and, relative to the latter, are assumed to possess similar mechanical properties. However, their simultaneous use at the Morrison Village site begs the question: do these two calcium carbonate tempers indeed possess similar mechanical properties? In order to assess their performance characteristics, a side-by-side controlled experimental test was conducted to determine the degree of similarity in providing increased vessel strength and toughness. METHODS Standardized ceramic test samples were systematically prepared via a set, explicit protocol. An Instron Series IX universal testing machine configured with a four-point flexural test jig was used to perform a flexural strength test of the test samples. The Instron load and deflection data were used to calculate three values related to mechanical performance: peak load, modulus of rupture, and modulus of elasticity. RESULTS All four comparative tests clearly show substantial differences in peak load, modulus of rupture, and modulus of elasticity. These differences are statistically significant for each performance attribute in every iteration of the experiment and as indicated by Mann-Whitney U Tests. CONCLUSIONS These results do not support the hypothesis that limestone and burnt shell offer the same performance characteristics. These results have implications for our understanding of prehistoric human selection of temper and the evolution of ceramic technology. Although both carbonate-based tempers are currently thought to offer the same benefits during the initial phase of pottery production, their contrasting post firing properties would have provided distinct benefits in different contexts. Future assessments of the Morrison Village ceramic assemblage should focus on residue analysis, or other functional indicators, to support or falsify this hypothesis.