Effect of two microshear test devices on bond strength and fracture pattern in primary teeth.

نویسندگان

  • Tamara Kerber Tedesco
  • Eugenio Jose Garcia
  • Fabio Zovico Maxnuck Soares
  • Rachel de Oliveira Rocha
  • Rosa Helena Miranda Grande
چکیده

This in vitro study evaluated the influence of two devices for application of shear load in microshear tests on bond strength and fracture pattern of primary enamel and dentin. Eighty primary molars were selected and flat enamel (40 teeth sectioned mesio-distally) and dentin (40 teeth sectioned transversally) surfaces were obtained. Both surfaces were polished to standardize the smear layer. Two-step etch-and-rinse adhesive systems (Adper Single Bond and XP Bond) were used. Polyethylene tubes was placed over the bonded surfaces and filled with composite resin. The microshear testing was performed after storage in water (24 h/37 °C) using two devices for application of microshear loads: a notched rod (Bisco Shear Bond Tester) or a knife edge (Kratos Industrial Equipment). Failure modes were evaluated using a stereomicroscope. Bond strength data were subjected to ANOVA and chi-square test to compare the failure mode distributions (α=0.05). No significant differences were observed between the groups for dentin and enamel bond strength or fracture patterns (p>0.05). The predominant failure mode was adhesive/mixed. In conclusion, the devices for application of shear loads did not influence the bond strength values, regardless of adhesive system and substrate.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Microshear Bond Strength of Glass Ionomer to Primary Dentin following Surface Treatment by Bur and Er,Cr:YSGG Laser

Background and Aim: Er,Cr:YSGG laser irradiation has been suggested as an effective method of cavity preparation and surface treatment to enhance the bond strength. The aim of this study was to assess the microshear bond strength of Fuji II LC glass ionomer (GI) cement to primary dentin following bur preparation and Er,Cr:YSGG irradiation. Materials and Methods: This in vitro, experimental stu...

متن کامل

Effect of adhesive layers on microshear bond strength of nanocomposite resin to dentin

BACKGROUND Bond strength of adhesive layer can absorb unwanted stresses of polymerization shrinkage in composite resin restorations; increased microshear bond strength can prevent failure of restoration materials, the purpose of this study was to evaluate the effect of adhesive layers on microshear bond strength of nanocomposite resin to dentin. MATERIAL AND METHODS Two different types of adh...

متن کامل

Shear Bond Strength of Composite to Primary Enamel Treated with Casein Phosphopeptide Amorphous Calcium Phosphate Using Total-Etch and Self-Etch Bonding Systems

Background and Aim: By application of casein phosphopeptide amorphous calcium phosphate (CPP-ACP) as a remineralizing agent, it may be feasible to only remove the carious dentin and better preserve the tooth structure. This study aimed to assess the shear bond strength of composite to primary enamel treated with CPP-ACP using total-etch and self-etch bonding systems. Materials and Methods: T...

متن کامل

بررسی اثر تعداد لایه‌های ادهزیو بر استحکام باند ریز برشی و ریز سختی سطح باند شده عاج پس از کاربرد چهار نوع ادهزیو

Background and Aims: In this in-vitro study, the effect of multiple adhesive coating on the microshear bond strength of composite to dentin and surface microhardness of dentin after treatment with four adhesives (One Step Plus, One Step, Single Bond, Single Bond 2) were evaluated. Materials and Methods: One hundred intact human molars were cut to obtain disks of dentin having 2 mm thickness. F...

متن کامل

تاثیر اسید هیدروفلوریک تجربی بر استحکام باند و ریزنشت کامپوزیت به پرسلن

Background and Aims: The aim of this study was to evaluate the quality of an experimental hydrofluoric acid (HF) for preparation of porcelain and to compare it with two commercial hydrofluoric acids in Iranian trademark. Materials and Methods: A- Evaluation of etch pattern of experimental HF using scanning electron microscope (SEM): 6 feldespathic discs were divided into 3 groups. Each group w...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:
  • Brazilian dental journal

دوره 24 6  شماره 

صفحات  -

تاریخ انتشار 2013