Soft magnetic properties of nanocrystalline Fe73B7Si16Nb3Cu1 alloy after rapid heating under tensile stress

نویسندگان

  • Anton Nosenko
  • Taras Mika
  • Olexandr Rudenko
  • Yevhenii Yarmoshchuk
  • Viktor Nosenko
چکیده

Amorphous Fe73B7Si16Nb3Cu1 ribbon was crystallized rapidly by electric current heating under simultaneously applied tensile stress along the ribbon axis. As a result, strong transverse magnetic anisotropy was induced in the ribbon. Dynamic magnetic properties of the ribbons rapidly heated either under the tensile stress or without tensile stress were measured using toroidal cores. Optimal electric current heating regime that provides maximum improvement of the initial magnetic permeability and core loss was determined. Tensile stress increase from 0 to 180 MPa was shown to result in the decrease of the initial magnetic permeability down to 400 and core loss at frequencies from 0.4 to 200 kHz. Comparative analysis of magnetic properties of the cut core (with non-magnetic gap) and the cores heated under tensile stress was carried out. The magnetic properties of the latter cores are advantageous for manufacturing the reactors and linear chokes of switch-mode power supplies.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

بررسی سینتیک نانو تبلور نوارهای نرم مغناطیس FINEMET در شرایط غیرهمدما

The soft magnetic nanocrystalline Fe73.5Si13.5B9Cu1Nb3 alloy (FINEMET®) is produced by heat treatment of amorphous precursor. Determining kinetic parameters of amorphous structure transformation to nanocrystalline allows the control of microstructure (e.g. size and volume fraction of nanocrystalline grains) in order to achieve desired soft magnetic properties by optimizing the heat treatment co...

متن کامل

INFLUENCE OF HEATING RATE ON MICROSTRUCTURE AND MAGNETIC PROPERTIES OF Fe3B/Nd2Fe14B NANOCOMPOSITE MAGNETS

The nanocomposite magnet, which is composed of exchange coupled nanocrystalline soft (Fe3B, α-Fe) and hard (Nd2Fe14B) magnetic phases, was first reported by Coehoorn et al. [1], and the theoretical basis of it was reported by Kneller and Hawig [2]. Nd-Fe-B based nanocomposite magnet has attracted considerable research interest due to its excellent magnetic properties with relatively low amount ...

متن کامل

Magnetic and Electrical Properties of Nanocrystalline Fe85Si10Ni5/Phenolic Resin Soft Magnetic Composites

In this work, nanocrystalline Fe85Si10Ni5 soft magnetic powders were prepared by mechanical alloying and subsequent annealing to reduce the internal stresses and lattice strains. The powders were mixed with phenolic resin and warm pressed to produce nanostructured soft magnetic composites. The effect of annealing time and temperature on the crystalline structure, microstructure and magnetic pro...

متن کامل

DC bias immune nanocrystalline magnetic cores made of Fe73Nb3Cu1B7Si16 ribbon with induced transverse magnetic anisotropy

The comparative analysis of magnetic properties of cut cores made of nanocrystalline Fe73Nb3Cu1B7Si16 alloy ribbon and cores made of the same ribbon with preliminary tension-induced transverse magnetic anisotropy was carried out. The possibility of improving magnetic properties of cut cores, decreasing loss, and increasing DC bias immunity of reversible magnetic permeability is presented. The i...

متن کامل

Production and Characterization of Nano Crystalline Fe85Si10Ni5 Soft Magnetic Alloys by Mechanical Alloying

Abstract There are various methods to produce iron based nano crystalline magnetic alloys. Among these methods, mechanical alloying is one of the most important. In this research, nano crystalline Fe85Si10Ni5 soft magnetic alloy was synthesized by mechanical alloying. The effect of alloying time on phase constituents and magnetic properties of the produced powders was investigated, by X-ray di...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 10  شماره 

صفحات  -

تاریخ انتشار 2015