Correlation between desorption of deuterium and recovery of irradiation defects in simultaneously deuterium and carbon ion-implanted tungsten
نویسندگان
چکیده
defects in simultaneously deuterium and carbon ion-implanted tungsten Rie KURATA, Makoto KOBAYASHI, Sachiko SUZUKI, Wanjing WANG, Naoko ASHIKAWA, Akio SAGARA, Naoaki YOSHIDA, Yasuhisa OYA, and Kenji OKUNO 1) Radioscience Research Laboratory, Faculty of Science, Shizuoka University, 836, Ohya, Suruga-ku, Shizuoka 422-8529, Japan 2) National Institute for Fusion Science, Japan 3) Institute of Applied Mechanics, Kyushu University, Japan
منابع مشابه
Structural Transformations in Austenitic Stainless Steel Induced by Deuterium Implantation: Irradiation at 295 K.
Deuterium thermal desorption spectra were investigated on the samples of austenitic steel 18Cr10NiTi pre-implanted at 295 K with deuterium ions in the dose range from 8 × 10(14) to 2.7 × 10(18) D/cm(2). The kinetics of structural transformation development in the steel layer was traced from deuterium thermodesorption spectra as a function of deuterium concentration. Three characteristic regions...
متن کاملEffects of zirconium element on the microstructure and deuterium retention of W–Zr/Sc2O3 composites
Dense W and W-Zr composites reinforced with Sc2O3 particles were produced through powder metallurgy and subsequent spark plasma sintering (SPS) at 1700 °C and 58 MPa. Results showed that the W-1vol.%Zr/2vol.%Sc2O3 composites exhibited optimal performance with the best relative density of up to 98.93% and high Vickers microhardness of approximately 583 Hv. The thermal conductivity of W-Zr/Sc2O3 ...
متن کاملImplantation Energy Dependence on Deuterium Retention Behaviors for the Carbon Implanted Tungsten
Yasuhisa Oya*, Makoto Kobayashi, Naoaki Yoshida, Naoko Ashikawa, Akio Sagara, Yuji Hatano, and Kenji Okuno 1) Radioscience Research Laboratory, Faculty of Science, Shizuoka University, 836, Ohya, Suruga-ku, Shizuoka 422-8529, Japan. 2) Institute for Applied Mechanics, Kyushu University, Fukuoka 816-8580, Japan. 3) National Institute for Fusion Science, Gifu 509-5292, Japan. 4) Hydrogen Isotope ...
متن کاملMolecular dynamics simulation of erosion and surface evolution of tungsten due to bombardment with deuterium and carbon in Tokamak fusion environments
The behavior of tungsten as plasma facing material in fusion environment is investigated using molecular dynamics simulation. Tungsten erosion and surface evolution is simulated during irradiation by carbon and deuterium ions. Non-cumulative pure carbon bombardment on crystal tungsten shows that substrate temperature does not affect carbon trapping rate, implantation depth, and tungsten sputter...
متن کاملDeuterium diffusion and retention in a tungsten-carbon multilayer system
A tungsten-carbon multilayer system deposited by magnetron sputtering was used as a model system to study deuterium diffusion in tungsten, carbon and related carbides. After deposition the as-deposited multilayer films were annealed at different temperatures to achieve different structures. The structural changes due to annealing were investigated by Rutherford backscattering spectrometry and X...