Influence of Fineness of Recycled Glass Waste and Slag on Compressive Strength of Sulphate Resisting Cement Mortars
نویسنده
چکیده
Method: At first, two optimized fineness levels were attained for both cement substituting materials used in this study (GGW as glass fine ˂ 38μm (GF), glass superfine ˂ 25μm (GSF) and EAFS as slag fine ˂ 75μm (SF), slag superfine ˂ 32μm (SSF)). In addition to control mortar (CM), four types of binary mortar mixtures were cast by substituting cement 5-20% with GGW (GF and GSF) and 10-30% with EAFS (SF and SSF). ASTM C109 and C311 were employed to perform compressive strength tests and to calculate the SAI values, respectively.
منابع مشابه
Influence of Mechanically Activated Electric Arc Furnace Slag on Compressive Strength of Mortars Incorporating Curing Moisture and Temperature Effects
In this study, the influence of mechanically activated electric arc furnace slag (EAFS) was investigated through compressive strength tests on 50 mm mortar cubes. The objective was to convert the wasteful EAFS into a useful binding material to reduce the cement content in concrete without compromising strength and economy. Four different groups of mortar were cast which include control mortar, ...
متن کاملEffects of Pozzolanic Admixture (Waste Bricks) on Mechanical Response of Mortar
This work presents an experimental study realized at the materials laboratory of the University of M’sila. It consists to vary the percentage of the pozzolanic admixture (waste bricks) in cement by the substitution method (partial replacement of the clinker by the calcined clay). The characteristics of cement at anhydrous state and the hydrated state (chemical composition, specific weight and f...
متن کاملRecovering industrial sludge-derived slag as fine aggregate.
This study presents the result of using melting to recover both industrial sludge slag (the main constituent of which is calcium fluoride) and water works sludge slag as fine aggregate in cement. The main characteristics of both slag and cement mortars were measured to evaluate the feasibility of using slag as aggregate. In this study, the slag replacement ratios were 0, 10, 20, 30, 40, and 50%...
متن کاملAging and Curing Temperature Effects on Compressive Strength of Mortar Containing Lime Stone Quarry Dust and Industrial Granite Sludge
In this study, the researchers investigated the potential use of locally available waste materials from the lime stone quarry and the granite industry as a partial replacement of cement. Quarry sites and granite industry in the eastern province of Saudi Arabia produces tons of powder wastes in the form of quarry dust (QD) and granite sludge (GS), respectively, causing serious environmental prob...
متن کاملEco-Friendly Hybrid Concrete using Pozzolanic Binder and Glass Fibers
Hybrid Concrete focused on the development of buildings, highways, and other structures of civil engineering. In the current study, various mix combinations have been prepared and tested with different percentages of super-plasticizer at different levels of water reduction for obtaining the optimum mix. Further, study on different properties of hybrid concrete and replacement of ordinary portla...
متن کامل