Metallography of Aluminium alloys
ثبت نشده
چکیده
This lecture aims at providing a survey of the metallographic techniques available for the examination of aluminium and its alloys. The information must be sufficient to be sure that the students and the users are able to choose the most suitable technique to solve their problems in the examination of samples. The lecture should contain a direct understanding of the main problems in the metallography of the different classes of aluminium materials.
منابع مشابه
Strengthening Mechanisms in the Aged 2024 and 7075 Aluminium Alloys
Aluminum 2024 and 7075 alloys which are widely used in aerospace and marine applications were chosen to investigate their strengthening mechanisms. Using differential thermal analysis (DIA), metallography and tension tests, the best solutionizing conditions were determined to be 500±5°C and 2 hours for 2024 and 480?±5°C and 1 hour for 7075 alloy. Aging was performed in the range of 100 to 200°C...
متن کاملThe Investigation of Modelling Material Behavior in Autofrettaged Tubes Made from Aluminium Alloys
Normal 0 false false false EN-US X-NONE AR-SA The ratio of compression yield strength to the initial tensile yield strength is called Bauschinger effect factor, BEF. A nonlinear strain hardening mathematical model is proposed for 7075 aluminium alloy (A7075). Uniaxial tension-compression experimental data are used to figure out a suitable model to study the BEF. Hence, uniaxial tension-co...
متن کاملINFLUENCE OF MECHANICAL ALLOYING AND LEAD CONTENT ON MICROSTRUCTURE, HARDNESS AND TRIBOLOGICAL BEHAVIOR OF 6061 ALUMINIUM ALLOYS
In the present work, one batch of prealloyed 6061Al powder was processed by mixing and another one was ball milled with varying amount of lead content (0-15 vol. %). These powders were compacted at 300MPa and sintered at 590˚C under N2. The instrumented hardness and the young’s modulus of as-sintered 6061Al-Pb alloys were examined as a function of lead content and processing route. The we...
متن کاملInvestigating the Effects of Cold Bulge Forming Speed on Thickness Variation and Mechanical Properties of Aluminum Alloys: Experimental and Numerical
In this work, cold bulge forming of an Aluminium-Magnesium (Al-Mg) sheet with a solid bulging medium is performed experimentally and numerically. Mechanical properties and thickness variations of Al-Mg sheet are evaluated before and after the forming process. The results indicated that the Al-Mg sheet has taken the desired shape without necking using the cold bulge forming process. Also, the...
متن کاملA Comparative Study of Aluminium Alloy and Titanium Alloy Comparison of AL-7175 alloy and Ti6Al4V alloy (Literature Survey Paper)
About 50% of metals used in Aerospace industries are Aluminium and Titanium alloys, Alloys such as Ti6Al4V, AL-7175, and AL7075 are used extensively in space vehicles, aviation, and automotive industries for having enhanced mechanical properties like High strength to weight ratio, low Thermal Expansion and better Corrosion resistance. Comparison of properties Aluminium and Titanium alloys shows...
متن کامل