Visible-light photochemical activity of heterostructured core-shell materials composed of selected ternary titanates and ferrites coated by tiO2.

نویسندگان

  • Li Li
  • Xuan Liu
  • Yiling Zhang
  • Noel T Nuhfer
  • Katayun Barmak
  • Paul A Salvador
  • Gregory S Rohrer
چکیده

Heterostructured photocatalysts comprised of microcrystalline (mc-) cores and nanostructured (ns-) shells were prepared by the sol-gel method. The ability of titania-coated ATiO3 (A = Fe, Pb) and AFeO3 (A = Bi, La, Y) catalysts to degrade methylene blue in visible light (λ > 420 nm) was compared. The catalysts with the titanate cores had enhanced photocatalytic activities for methylene blue degradation compared to their components alone, whereas the catalysts with ferrite cores did not. The temperature at which the ns-titania shell is crystallized influences the photocatalytic dye degradation. mc-FeTiO3/ns-TiO2 annealed at 500 °C shows the highest reaction rate. Fe-doped TiO2, which absorbs visible light, did not show enhanced photocatalytic activity for methylene blue degradation. This result indicates that iron contamination is not a decisive factor in the reduced reactivity of the titania coated ferrite catalysts. The higher reactivity of materials with the titanate cores suggests that photogenerated charge carriers are more easily transported across the titanate-titanate interface than the ferrite-titanate interface and this provides guidance for materials selection in composite catalyst design.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Visible light photochemical activity of heterostructured PbTiO3–TiO2 core–shell particles

Heterostructured powders composed of microcrystalline PbTiO3 cores coated with nanostructured TiO2 shells were prepared by a sol–gel method. When exposed to visible light (l 4 420 nm), the heterostructured powder degrades methylene blue at a rate 4.8 times greater than PbTiO3, TiO2, or mechanical mixtures of the phases. The rate at which the heterostructured powder degrades methylene blue depen...

متن کامل

Heterostructured (Ba,Sr)TiO3/TiO2 core/shell photocatalysts: Influence of processing and structure on hydrogen production

Heterostructured powders composed of microcrystalline (mc-) BaTiO3 and SrTiO3 cores coated with nanostructured (ns-) TiO2 shells were prepared using a solegel method. The influences of annealing temperature, coating thickness, cocatalyst loading, and core size on photocatalytic hydrogen production were experimentally determined. The amount of hydrogen produced depends on the annealing temperatu...

متن کامل

Photocatalyst Ag@N/TiO2 Nanoparticles: Fabrication, Characterization, and Investigation of the Effect of Coating on Methyl Orange Dye Degradation

In this research, N-doped TiO2 (N/TiO2) nanoparticles have been synthesized by a sol-gel method. N/TiO2 nanoparticle has been coated with Ag metal by photochemical method. Triethylamine, N(CH3CH2)3, have been used as precursors of Nitrogen, titanium tetraiso-propoxide (TTIP), Ti[OCH(CH3)2]4, used as precursors of titanium and Ag(NO3)2 used as precursors of Silver in synthesis of these nanoparti...

متن کامل

Heterostructured Ceramic Powders for Photocatalytic Hydrogen Production: Nanostructured TiO2 Shells Surrounding Microcrystalline (Ba,Sr)TiO3 Cores

Heterostructured photocatalysts were prepared to have nanostructured (ns) TiO2 shells surrounding microcrystalline (mc) cores of (Ba,Sr)TiO3. The as-prepared heterostructures were annealed between 400°C and 600°C to improve crystallinity and core-shell interfacial bonding. X-ray diffraction, electron microscopy, and gas adsorption measurements demonstrated that 50 nm thick shells composed of na...

متن کامل

Preparation of Cr-doped TiO2 thin film by sonochemical/CVD method and its visible light photocatalytic activity for degradation of paraoxon

In this work, nanostructured TiO2 and Cr-doped TiO2 thin films were deposited on glass substrate through sonochemical-chemical vapor deposition (CVD) method. The resulting thin films were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), UV-visible absorption spectroscopy, and photoluminescence spectroscopy techniques. The TiO2 thin film has nanocubic morphology and ...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:
  • ACS applied materials & interfaces

دوره 5 11  شماره 

صفحات  -

تاریخ انتشار 2013